Method for preparing sintered NdFeB magnets

A method for preparing sintered NdFeB magnets, the method including the steps of:

• a) Preparing alloy flakes from a raw material of the NdFeB magnet by strip casting, then performing a hydrogen decrepitation of the alloy flakes to produce alloy pieces, then pulverization the alloy pieces to an alloy powder by jet mill, and finally performing molding and orientation, cold isostatic pressing, and then get a green compact;
• b) Putting the green compact into a vacuum furnace and performing a first sintering step, wherein the sintering temperature is in the range of 830° C. to 880° C. for 2 to 10 hours and the pressure in the furnace is 5×10−1 Pa or less, and a density of the green compact being in the range of 7.08 to 7.37 g/cm3 after the first sintering step;
• c) Performing a second sintering step while applying a pressure along the magnetic orientation direction of the green compact achieved by step b), wherein the pressure applied on the green compact is in the range of 1 MPa to 5 MPa and the sintering temperature is in the range of 720° C. to 850° C. for 15 to 60 minutes, and wherein the temperature of the first sintering step is at least 10° C. higher than the temperature of the second sintering step;
• and
• d) Subjecting the sintered magnet of step c) to an annealing treatment.