Ferritic stainless steel sheet and method of producing same, and al or al alloy coated stainless steel sheet

A method of producing a ferritic stainless steel sheet comprising a chemical composition containing, in mass %,

• C:
• 0.030% or less,
• Si:
• 3.0% or less,
• Mn:
• 1.0% or less,
• P:
• 0.040% or less,
• S:
• 0.010% or less,
• Cr:
• 11.0% to 30.0%,
• Al:
• 10.7% to 20.0%,
• Ni:
• 0.05% to 0.50%,
• N:
• 0.020% or less, and
• at least one selected from the group consisting of Zr:
• 0.01% to 0.20% and Hf:
• 0.01% to 0.20%, and
• one or more selected from the group consisting of
• REM:
• 0.01% to 0.20%,
• Cu:
• 0.01% to 0.10%,
• Ti:
• 0.01% to 0.50%,
• Nb:
• 0.01% to 0.50%,
• V:
• 0.01% to 0.50%,
• Mo:
• 0.01% to 6.0%,
• W:
• 0.01% to 6.0%,
• B:
• 0.0001% to 0.0050%,
• Ca:
• 0.0002% to 0.0100%, and
• Mg:
• 0.0002% to 0.0100%,
• with a balance being Fe and inevitable impurities, the method comprising subjecting an Al or Al alloy coated stainless steel sheet comprising:
• a coating substrate;
• and
• an Al or Al alloy coated layer on a surface of the coating substrate,
• wherein the coating substrate is a ferritic stainless steel sheet having a chemical composition containing, in mass %,
• C:
• 0.030% or less,
• Si:
• 1.0% or less,
• Mn:
• 1.0% or less,
• P:
• 0.040% or less,
• S:
• 0.010% or less,
• Cr:
• 11.0% to 30.0%,
• Al:
• 2.5% to 6.5%,
• Ni:
• 0.05% to 0.50%,
• N:
• 0.020% or less,
• at least one selected from the group consisting of Zr:
• 0.01% to 0.20% and Hf:
• 0.01% to 0.20%, and
• one or more selected from the group consisting of
• REM:
• 0.01% to 0.20%,
• Cu:
• 0.01% to 0.10%,
• Ti:
• 0.01% to 0.50%,
• Nb:
• 0.01% to 0.50%,
• V:
• 0.01% to 0.50%,
• Mo:
• 0.01% to 6.0%,
• W:
• 0.01% to 6.0%,
• B:
• 0.0001% to 0.0050%,
• Ca:
• 0.0002% to 0.0100%, and
• Mg:
• 0.0002% to 0.0100%,
• with a balance being Fe and inevitable impurities, and
• a thickness and an Al content of the coating substrate and a thickness of the Al or Al alloy coated layer satisfy a relationship in the following expression (1):
• 8.0≤CAl+30×t/T≤20.0 (1)
• where CAl is the Al content of the coating substrate in mass %, T is the thickness of the coating substrate in μm, and t is the thickness of the Al or Al alloy coated layer in μm, and, in the case where the Al or Al alloy coated layer is present on each of both sides of the coating substrate, is a total thickness of Al or Al alloy coated layers on the both sides of the coating substrate, to a heat treatment of holding in a temperature range of 600° C. to 1300° C. for 1 minute or more and 120 minutes or less in a vacuum of 1×10−1 Pa or less or a non-oxidizing atmosphere, and
• wherein the number of times the heat treatment is performed is 1.