US 11,767,237 B2 · Method for preparing amorphous molybdenum oxide adsorption material and application thereof

Abstract

The invention relates to a method for preparing amorphous molybdenum oxide adsorption material and an application thereof. The invention aims to solve the technical problem of low recovery efficiency of silver ions in coexisting silver-containing wastewater in the prior art. The method of the present invention includes:1) preparation of electrolyte; and 2) subjecting to cyclic voltammetry. The amorphous molybdenum oxide adsorption material prepared by the present invention is used as an adsorbent for adsorbing and reducing silver ions in wastewater. The invention successfully prepares amorphous molybdenum oxide (MoOx) by cyclic voltammetry, which has a highly selective reduction adsorption for Ag+. Silver ions and the adsorbent MoOx could be subjected to redox reaction to remove silver ions in water. The removal efficiency of the silver ions in wastewater by the amorphous molybdenum oxide prepared by cyclic voltammetry of the invention is up to 99.85%.

Claims5

Dependent claims

A method for preparing an amorphous molybdenum oxide adsorption material as an adsorbent for adsorbing and reducing silver ions, which is carried out by the following steps:

1) Preparation of an electrolyte:
mixing ammonium molybdate and sodium sulfate together in water, and stirring ultrasonically for 5 min to 10 min to obtain a mixed solution, wherein in the mixed solution, the concentration of ammonium molybdate is 2 mmol/L to 2.5 mmol/L, and that of sodium sulfate is 0.5 mol/L to 0.6 mol/L;
and
2) Subjecting to cyclic voltammetry:
connecting an electrochemical workstation, and subjecting the mixed solution prepared in step 1) as the electrolyte to electrodeposition for 25 to 30 cycles by cyclic voltammetry to obtain the amorphous molybdenum oxide adsorption material, wherein the cyclic voltammetry has the potential window of −0.09 V to −1.29 V and the sweep speed of 50 mV/s to 60 mV/s.

2 more elements

Dependencies are inferred from the claim text.

Method for preparing amorphous molybdenum oxide adsorption material and application thereof

Life of this patent

Method for preparing amorphous molybdenum oxide adsorption material and application thereof

Life of this patent

Abstract

Claims5