Processing technology for inhibiting weld coarse grains of magnesium alloy profiles
AssigneeShandong University
InventorsLiang Chen, Jianwei Tang, Zhigang Li, Guoqun Zhao, Cunsheng Zhang
Life of this patent
Estimating the term…
Abstract
Disclosed is a processing technology for inhibiting weld coarse grains of magnesium alloy profiles, including the following steps: preparation of a magnesium alloy ingot, homogenization, scalping, extrusion, pre-stretching at room temperature, solution treatment, quenching, stretching correction, artificial aging, etc. The processing technology can effectively control the production of weld coarse grains in extrusion and heat treatment processes of magnesium alloy profiles, and all property indexes of final products are higher than standard requirements.
Claims4
A processing technology for inhibiting weld coarse grains of magnesium alloy profiles, comprising the following steps:
- (1) preparing a magnesium alloy ingot, wherein a size of the ingot needs to be selected according to an extruder used;
- (2) homogenizing the magnesium alloy ingot;
- (3) scalping the magnesium alloy ingot obtained in step (2);
- (4) extruding the magnesium alloy ingot obtained in step (3) to obtain a magnesium alloy extruded profile, and at the same time, cooling an extrusion die by using liquid nitrogen during extrusion;
- (5) pre-stretching the extruded profile obtained in step (4) at room temperature;
- (6) performing solution treatment on the magnesium alloy profile pre-stretched in step (5), and quenching the magnesium alloy profile after the solution treatment is completed;
- (7) performing stretching correction on the magnesium alloy profile after the solution treatment in step (6);
- and
- (8) artificially aging the profile obtained in step (7), wherein
- in step (5), a pre-stretching deformation at room temperature is 10-20%,
- in step (4), a temperature of the magnesium alloy ingot is 250-350° C., a temperature of the die is 280-380° C., a temperature of an extrusion cylinder is 260-360° C., an extrusion speed is 0.5-5 mm/s, and an outlet pressure of the liquid nitrogen is 0.5-0.6 MPa,
- in step (6), a solution treatment temperature is 380-420° C., and a solution treatment time is 1-3 h,
- in step (7), a stretching deformation of the stretching correction is 0.5-1.5%,
- in step (8), an aging temperature is 98-225° C., and an aging time is 12-144 h.
Dependencies are inferred from the claim text.