Lower pyrolysis temperature binder for silicon-dominant anodes

Abstract

Systems and methods are provided for carbon additives for direct coating of silicon-dominant anodes. An example composition for use in directly coated anodes may include a silicon-dominated anode active material, a carbon-based binder, and a carbon-based additive, with the composition being configured for low-temperature pyrolysis. The low-temperature pyrolysis may be conducted at <600° C. An anode may be formed using a direct coating process of the composition on a current collector. The anode active material yields silicon constituting between 86% and 97% of weight of the formed anode after pyrolysis. The carbon-based additive yields carbon constituting between 2% and 6% of weight of the formed anode after pyrolysis.