Sliding member
AssigneeNippon Piston Ring Co., Ltd.
InventorsNoriaki Chida, Shota Seki
Life of this patent
Estimating the term…
Abstract
To provide a sliding member, such as a piston ring for an internal combustion engine, having low friction and excellent toughness. The above-described problem is solved by a sliding member (10) such as a piston ring coated with a Cr—B—Ti—V—(Mn, Mo)—N-based alloy film (2) on a sliding surface (11) thereof, and configured so that the alloy film (2) contains one or both of Mn and Mo and has a total content of the Mn and the Mo within a range of 2 mass % or less. Preferably, a B content is within a range of 0.1 mass % to 1.5 mass %, inclusive, a V content is within a range of 0.05 mass % to 1 mass %, inclusive, and a Ti content is within a range of 0.05 mass % to 1.5 mass %, inclusive.
Claims8
A sliding member comprising:
- a sliding surface coated with a Cr—B—Ti—V—(Mn, Mo)—N-based alloy film containing one or both of Mn and Mo and having a total content of the Mn and the Mo within a range of 0.1-2 mass %,
- a B content is within a range of 0.1 mass % to 1.5 mass %, inclusive, a V content is within a range of 0.05 mass % to 1 mass %, inclusive, and a Ti content is within a range of 0.05 mass % to 1.5 mass %, inclusive, and
- an N content is within a range of 30 mass % to 40 mass %, inclusive, and a remnant includes Cr and inevitable impurities;
- wherein
- a toughness evaluation value of a Cr—N alloy coating without B—Ti—V—(Mn,Mo) is 1;
- the toughness evaluation value of said Cr—B—Ti—V—(Mn,Mo)—N alloy coating is 1.41 to 1.59,
- the toughness evaluation value is the value obtained by multiplying a hardness ratio by a scratch ratio, wherein the hardness ratio is expressed as a relative value of the Vickers hardness value of the Cr—B—Ti—V—(Mn,Mo)—N alloy coating when the Vickers hardness of the Cr—N alloy coating without B—Ti—V—(Mn,Mo) is 1, and the scratch ratio is expressed as a relative value of the scratch ratio of the Cr—B—Ti—V—(Mn,Mo)—N alloy coating when the scratch ratio of the Cr—N alloy coating without B—Ti—V—(Mn,Mo) is 1,
- said Vickers hardness is measured by a Vickers hardness tester in accordance with the standards JIS B 7725, ISO 6507 HV(0.05), and
- the scratch ratio is measured using a scratch test device to determine a limit load at which peeling of the alloy film occurs when a force is applied parallel to the alloy film on a table at a table speed of 10 mm/min, and
- the scratch test device comprises an indenter having a load loading speed of 100 N/min, indenter tip R of 0.2 mm, and test load of 0 to 100N;
- the alloy film is pressed against a test specimen of SKH51;
- and the scratch ratio is determined from a scratch load measured by an AE (acoustic emission) generation detected by an AE detector with a sensitivity of 1.2 when the test specimen is moved a distance of 5 m.
Dependencies are inferred from the claim text.