Lead free frangible iron bullets
AssigneeTPI Powder Metallurgy, Inc.
InventorsStuart Yntema, Steven B. Yntema, Ted R. Easlick, David J. May
Life of this patent
Estimating the term…
Abstract
The invention relates to bullets having increased frangibility (or which can be easily fragmented) and to powder materials and processes for the manufacture of such bullets. The bullets of the present invention are made from an iron alloy containing 75-81% Hoeganaes MH-100 Iron 0.6-0.09% Carbon, and balance of admixed Copper powder. Said bullets are then coated for lubricity so the bullet does not prematurely wear the barrel of a gun. Additionally, the invention provides a simple low cost process to make bullets that is amenable to mass production via automation.
Claims7
A frangible bullet consisting of 75-81% sponge Iron with a particle size less than 100 mesh but substantially greater than 325 mesh 0.6-0.9% Carbon, and balance of an amount of Copper which is sintered into a final bullet at a controlled temperature of greater than 1475° F. for allowing the carbon to diffuse into the iron and oxygen free environment to allow for the carbon to at least partially alloy with—the sponge iron wherein the temperature is less than the melting point of copper of 1970° F. which does not allow for alloying with the copper but leaves the copper in a unmelted state allowing the copper to fill the voids between the sponge iron particles so as to produce a bullet capable of fragmenting upon impact with a target wherein the particle size limits iron particle to iron particle mechanical bonds at molding, which then also limits the particle bonds present in sintered bullet, thereby enhancing frangibility.
A method of making a frangible bullet which comprises pressing a powder comprising 75-81% sponge Iron with a particle size less than 100 mesh but substantially greater than 325 mesh 0.6-0.9% Carbon, and balance of an amount of Copper powder which is sintered into a final bullet at a controlled temperature of greater than 1475° F. for allowing the carbon to diffuse into the iron and oxygen free environment to allow for the carbon to at least partially alloy with the sponge iron wherein the temperature is less than the melting point of copper of about 1970° F. which does not allow for alloying of the sponge iron with the copper but leaves the copper in an unmelted state allowing the copper to fill the voids between the sponge iron particles so as to produce a bullet capable of fragmenting upon impact with a target in a die to form a pressed powder compact and subsequently sintering said pressed powder compact, wherein the sintering is performed in a protective hydrogen/nitrogen atmosphere at a temperature ranging from 1725° F. to 1800° F. fora length of time from 10 to 15 minutes at temperature;
- and
- wherein the particle size limits iron particle to iron particle mechanical bonds at molding, which then also limits the particle bonds present in sintered bullet, thereby enhancing frangibility.
Dependencies are inferred from the claim text.