US 11,640,986 B2Granted
Implantation and annealing for semiconductor device
AssigneeTaiwan Semiconductor Manufacturing Company, Ltd.
InventorsYu-Chang Lin, Tien-Shun Chang, Szu-Ying Chen, Chun-Feng Nieh, Sen-Hong Syue, Huicheng Chang
Life of this patent
Estimating the term…
Abstract
A semiconductor device, and a method of manufacturing, is provided. A dummy gate is formed on a semiconductor substrate. An interlayer dielectric (ILD) is formed over the semiconductor fin. A dopant is implanted into the ILD. The dummy gate is removed and an anneal is performed on the ILD. The implantation and the anneal lead to an enhancement of channel resistance by a reduction in interlayer dielectric thickness and to an enlargement of critical dimensions of a metal gate.
Claims20
A method comprising:
- forming a dummy gate layer on a semiconductor substrate;
- depositing a mask layer over the dummy gate layer;
- forming a dummy gate and a mask over the dummy gate by patterning the mask layer and the dummy gate layer;
- forming a dielectric layer over the dummy gate and the mask;
- performing a first planarization on the dielectric layer, a top surface of the dielectric layer being level with a top surface of the mask after the first planarization;
- removing the mask with an etch back process;
- performing a second planarization on the dielectric layer, a top surface of the dielectric layer being level with a top surface of the dummy gate after the second planarization;
- implanting a dopant into a top portion of the dielectric layer, wherein a bottom portion of the dielectric layer remains substantially free of the dopant, the bottom portion being below the top portion;
- after implanting the dopant, removing the dummy gate;
- and
- after removing the dummy gate, performing an anneal on the dielectric layer.
8 more elements
A method comprising:
- forming a dummy gate over a fin and a mask over the dummy gate, the fin extending from a semiconductor substrate;
- depositing a dielectric layer over the dummy gate, the mask, and the fin;
- performing a first anneal on the dielectric layer;
- planarizing the dielectric layer to be level with a top surface of the mask;
- performing an etch back process, the etch back process removing the mask;
- planarizing the dielectric layer to be level with a top surface of the dummy gate;
- implanting nitrogen into the dielectric layer;
- removing the dummy gate to form a first recess;
- after removing the dummy gate, performing a second anneal on the dielectric layer, wherein after the second anneal, the nitrogen is distributed in the dielectric layer to a first depth, the first depth being in a range of 5 nm to 15 nm, the dielectric layer being substantially free of nitrogen below the first depth;
- and
- forming a gate electrode in the first recess.
8 more elements
A method comprising:
- forming a dielectric layer over a mask, the mask being over a dummy gate, the dummy gate being on a channel region of a semiconductor fin;
- annealing the dielectric layer;
- after annealing the dielectric layer, removing a portion of the dielectric layer above the mask with a chemical mechanical polish;
- after removing the portion of the dielectric layer, removing the mask;
- performing a planarization on the dielectric layer, wherein after the planarization a top surface of the dielectric layer is level with a top surface of the dummy gate;
- forming an implanted region in an upper region of the dielectric layer, the forming the implanted region comprising an implantation of the upper region with a first dopant, an unimplanted region of the dielectric layer below the implanted region being substantially free of the first dopant after the implantation;
- removing the dummy gate, the removing the dummy gate exposing a top surface of the channel region;
- shrinking the dielectric layer in a vertical dimension perpendicular to the top surface of the channel region;
- and
- forming a gate stack on the top surface of the channel region, the gate stack extending through the dielectric layer, the gate stack having a top width and a bottom width, the top width being larger than the bottom width.
7 more elements