Iron oxide pigments containing Al

A process for producing aluminium-containing haematite pigments of formula

• Fe2-xAlxO3 with x values from 0.01 to 0.25, wherein the pigments possess an a* value of 30.5 to 32.5 CIELAB units and a b* value of 25.5 to 30.5 CIELAB units, and Al-containing iron oxides have a saturation Cab* of 39.8 to 44.6 CIELAB units, measured in each case as full shade in the alkyd resin according to DIN EN ISO 787-25:2007, comprising at least the steps of a) precipitation, b) oxidation and c) calcination, wherein:
• a1) an aqueous solution comprising ions of iron, of sulfate and of aluminium, a molar ratio of iron ions to Al ions being 199:1 to 7:1, is reacted with sodium hydroxide NaOH, as an alkaline compound, with the aqueous solution comprising ions of iron, of sulfate and of aluminium being metered into an initial charge of the alkaline compound, or
• a2) an aqueous solution comprising ions of iron and of sulfate is reacted with sodium hydroxide NaOH, as an alkaline compound, and with at least one alkali metal aluminate aluminium compound, with the molar ratio of iron in the solution to aluminium in the aluminium compound being 199:1 to 7:1 and with the alkaline compound being introduced as an initial charge with the at least one alkali metal aluminate aluminium compound, and the aqueous solution comprising ions of iron and of sulfate being metered in,
• b) an aqueous suspension obtained after step a1) or a2) is oxidized in the presence of an oxidizing agent, and
• c) an oxidation product obtained after b) is calcined at a temperature of 500 to 1100° C. in an oxidizing atmosphere.