Binder-free and fouling-resistant CNT thin film membrane
Assignee4th Phase Water Technologies, Inc.
InventorChunhong Li
Life of this patent
Estimating the term…
Abstract
A hydrophilic graphitic material is provided that may be formed by heating a graphitic material to a temperature between about 150° C. to about 1400° C. for an extended period of time under an inert atmosphere. Annealing CNT film at 500 to 1400 removes amorphous carbon to produce purified CNT film. The purified CNT film can be further densified with the treatment of alkylphosphonic acid or alkyldiphophonic acid and heating to produce a hydrophilic, densified CNT film which is mechanically robust and does not adhere to other solid surfaces. These films can be used as filtration membranes with superior membrane fouling resistance among other uses.
Claims18
A process of densifying a carbon nanotube (CNT) film, comprising heating a CNT film prepared from a floating catalyst chemical vapor deposition (FCCVD) method to a temperature between about 600° C. and about 1200° C. under inert atmosphere for a period of time thereby removing amorphous carbon to produce a purified CNT film;
- densifying the purified CNT film by contacting the purified CNT film with an alkylphosphonic acid having the formula:
- CnH2n+1PO3H2, wherein n is an integer ranging from 1-18, and heating the purified film to a temperature between about 120° C. and about 200° C. for at least about 10 hours to form a densified CNT film;
- and
- heating the densified CNT film to a temperature between about 450° C. and 1000° C. under inert atmosphere.
A process of densifying a carbon nanotube (CNT) film, comprising:
- heating a CNT film to a temperature between about 600° C. and about 1200° C. under inert atmosphere for a period of time thereby removing amorphous carbon to produce a purified CNT film;
- densifying the purified CNT film by contacting the purified CNT film with an alkyldiphosphonic acid having the formula:
- H2O3P(CH2)nPO3H2, wherein n is an integer of 6-18 at a temperature between about 120° C. and about 200° C. for at least about 10 hours to form a densified CNT film.
A process of purifying densifying a carbon nanotube (CNT) film, comprising:
- heating a CNT film to a temperature between about 600° C. and about 1200° C. under inert atmosphere for a period of time thereby removing amorphous carbon to produce a purified CNT film;
- densifying the purified CNT film by contacting the purified CNT film with an alkylphosphonic acid having the formula:
- CnH2n+1PO3H2, wherein n is an integer ranging from 6-18,
- heating the purified CNT film to a temperature between about 120° C. and about 200° C. for at least about 10 hours to form a densified CNT film;
- heating the densified CNT film to a temperature between about 450° C. and 1000° C. under inert atmosphere.
Dependencies are inferred from the claim text.