Hot-dip coated steel sheet

A method for manufacturing a hot-dip coated steel sheet, the method comprising:

• A. providing a steel sheet having the following chemical composition in weight percent:
• 0.05≤C≤0.20%,
• 1.5≤Mn≤3.0%,
• 0.10≤Si≤0.45%,
• 0.10≤Cr≤0.60%,
• Al≤0.20%,
• V<0.005%
• and on a purely optional basis, one or more elements including:
• P<0.04%,
• Nb≤0.05%,
• B≤0.003%,
• Mo≤0.20%,
• Ni≤0.1%,
• Ti≤0.06%,
• S≤0.01%
• Cu≤0.1%,
• Co≤0.1%,
• N≤0.01%,
• a remainder of the composition being made of iron and inevitable impurities resulting from processing;
• B. recrystallization annealing the steel sheet in a full radiant tube furnace comprising a heating section, a soaking section, and a cooling section, and optionally an equalizing section, the recrystallization annealing including the following sub-steps:
• i. heating the steel sheet from ambient temperature to a temperature T1 between 700 and 900° C. in the heating section having an atmosphere A1 including from 0.1 to 15% by volume of H2 and an inert gas whose a dew point DP1 is between −18° C. and +8° C.,
• ii. soaking the steel sheet from T1 to a temperature T2 between 700 and 900° C. in the soaking section having an atmosphere A2 identical to A1 with a dew point DP2 equal to DP1, and
• iii. cooling the steel sheet from T2 to T3 between 400 and 700° C. in the cooling section having an atmosphere A3 including from 1 to 30% H2 by volume and an inert gas whose a dew point DP3 is below or equal to −30° C., and
• iv. optionally, equalizing the steel sheet from a temperature T3 to a temperature T4 between 400 and 700° C. in the equalizing section having an atmosphere A4 including from 1 to 30% H2 by volume and an inert gas whose a dew point DP4 is below or equal to −30° C.;
• and
• C. hot-dip coating of the annealed steel sheet in a bath based on zinc or based on aluminum.