Tough, high temperature polymers produced by stereolithography

#The present invention concerns polymerizable liquids, polymer compositions formed therefrom, and methods of making such polymer compositions, preferably in the form of shaped three-dimensional objects by additive manufacturing techniques such as continuous liquid interface production.

#In conventional additive or three-dimensional fabrication techniques, construction of a three-dimensional object is performed in a step-wise or layer-by-layer manner. Typically, layer formation is performed through solidification of photo curable resin under the action of visible or UV light irradiation. Generally referred to as “stereolithography,” two particular techniques are known: one in which new layers are formed at the top surface of the growing object; the other in which new layers are formed at the bottom surface of the growing object. Examples of such methods include those given in U.S. Pat. No. 5,236,637 to Hull (see, e.g., FIGS. 3-4), U.S. Pat. Nos. 5,391,072 and 5,529,473 to Lawton, U.S. Pat. No. 7,438,846 to John, U.S. Pat. No. 7,892,474 to Shkolnik, U.S. Pat. No. 8,110,135 to El-Siblani, U.S. Patent Application Publication No. 2013/0292862 to Joyce, and US Patent Application Publication No. 2013/0295212 to Chen et al.

#Recently, techniques referred to as “continuous liquid interface production” (or “CLIP”) have been developed. These techniques enable the rapid production of three-dimensional objects in a layerless manner, by which the parts may have desirable structural and mechanical properties. See, e.g., J. DeSimone et al., PCT Application Nos. PCT/US2014/015486 (published as U.S. Pat. No. 9,211,678); PCT/US2014/015506 (published as U.S. Pat. No. 9,205,601), PCT/US2014/015497 (published as U.S. Pat. No. 9,216,546), J. Tumbleston, et al., Continuous liquid interface production of 3D Objects, Science 347, 1349-1352 (published online 16 Mar. 2015), and R. Janusziewcz et al., Layerless fabrication with continuous liquid interface production, Proc. Natl. Acad. Sci. USA 113, 11703-11708 (Oct. 18, 2016).

#FIG. 1 shows a comparison of notched impact, HDT & Modulus (represented by dot size) between prior and new resin formulations. FPU=flexible polyurethane, RPU=rigid polyurethane; EPX=epoxy; CE=cyanate ester, HIS-HDR=high strength, heat deflection resistant.

#The present invention is now described more fully hereinafter with reference to the accompanying drawings, in which embodiments of the invention are shown. This invention may, however, be embodied in many different forms and should not be construed as limited to the embodiments set forth herein; rather these embodiments are provided so that this disclosure will be thorough and complete and will fully convey the scope of the invention to those skilled in the art.

#As used herein, the term “and/or” includes any and all possible combinations or one or more of the associated listed items, as well as the lack of combinations when interpreted in the alternative (“or”).

#Unless otherwise defined, all terms (including technical and scientific terms) used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs. It will be further understood that terms, such as those defined in commonly used dictionaries, should be interpreted as having a meaning that is consistent with their meaning in the context of the specification and claims and should not be interpreted in an idealized or overly formal sense unless expressly so defined herein. Well-known functions or constructions may not be described in detail for brevity and/or clarity.