Method for preparing all-solid-state photonic crystal fiber preforms by extrusion

A method for preparing all-solid-state photonic crystal fiber preform by extrusion, comprising:

• Step-1:
• preparing an extrusion container, an extrusion chamber, a core outlet mold, a first jacking rod having a first jacking end, a second jacking rod having a second jacking end, an extrusion head and a fiber preform outlet mold, wherein the extrusion container has an opening and a preform outlet respectively on the top and the bottom of the extrusion container;
• the extrusion chamber has a top opening and a bottom opening respectively on the top and the bottom of the extrusion chamber;
• the core outlet mold has a plurality of core outlets;
• the bottom opening of the extrusion chamber communicates with the plurality of core outlets on the core outlet mold;
• the size of the top opening of the extrusion chamber is smaller than the diameter of the first jacking end of the first jacking rod, and the size of the top opening is greater than the diameter of the second jacking end of the second jacking rod;
• Step-2:
• preparing a core glass ingot and a cladding glass ingot which are rinsed with alcohol and dried, wherein the core glass ingot has an outer diameter matched with an inner diameter of the extrusion chamber;
• and the cladding glass ingot has an outer diameter matched with an inner diameter of the extrusion container;
• Step-3:
• placing the cladding glass ingot inside the bottom of the extrusion container, placing the core glass ingot and the extrusion head inside the extrusion chamber, and mounting the core outlet mold at the bottom of the extrusion chamber, the core outlet mold is located above the cladding glass ingot and the extrusion head is located on the core glass ingot;
• Step-4:
• putting the extrusion chamber with the core glass ingot into the extrusion container, and resting the first jacking end of the first jacking rod against the top surface of the extrusion chamber, aligning the center of the first jacking end of the first jacking rod with the center of the core outlet mold;
• Step-5:
• heating the extrusion container with the extrusion chamber of Step-4 until the temperature in the extrusion container reaches a preset temperature T, so as to make the core glass ingot and the cladding glass ingot in the extrusion container soft to obtain softened core glass and cladding glass;
• wherein the preset temperature T is higher than Tg and lower than Tx;
• Tg is defined as the highest one of the core glass transition temperature and the cladding glass transition temperature, and Tx is defined as the lowest one of the core glass crystallization temperature and the cladding glass crystallization temperature;
• Step-6:
• pressing the first jacking rod against the top of the extrusion chamber, and pushing the extrusion chamber into the cladding glass inside the extrusion container, so as to make the bottom of the core outlets of the core outlet mold flush with the bottom of the softened cladding glass or make each bottom of the plurality of core outlets of the core outlet mold lower than the bottom of the softened cladding glass;
• Step-7:
• maintaining the temperature inside the extrusion container at the preset temperature T, taking the first jacking rod out of the extrusion container, and putting the second jacking rod into the extrusion container, in such a way that the second jacking end of the second jacking rod runs through the top opening of the extrusion chamber and resists against the extrusion head;
• Step-8:
• making the second jacking rod push the extrusion head to press the softened core glass inside the extrusion chamber, so that the softened core glass is extruded out from the plurality of core outlets on the core outlet mold located on the bottom of the extrusion container, obtaining a core array having N cores, where N is the number of cores extruded from the extrusion container when the second jacking rod pushes on the extrusion head;
• Step-9:
• uniformly pressing the softened core glass in the extrusion chamber and the softened cladding glass in the extrusion container, so that the softened core glass and softened cladding glass are co-extruded out from the preform outlet on the extrusion container, obtaining an initial product of the fiber preform;
• and
• Step-10:
• annealing the obtained initial product of the fiber preform at the transition temperature Tg for a preset period of time, and cooling the initial product of the fiber preform to room temperature, then a fiber preform is obtained,
• wherein a top plate is disposed in the extrusion chamber covering the core glass ingot;
• and the extrusion head has a plurality of extrusion stems corresponding to each core outlet on the core outlet mold and capable of inserting into the corresponding core outlet after passing through the top plate.