Fiber reinforced thermoplastic resin molded article and fiber reinforced thermoplastic resin molding material

A fiber reinforced thermoplastic resin molding material comprising inorganic fibers (A), organic fibers (B), a thermoplastic resin (C), and a component (D) having a melt viscosity at 200° C. lower than that of the thermoplastic resin (C), wherein

• the inorganic fibers (A) are carbon fibers,
• the fiber reinforced thermoplastic resin molding material comprises 5 to 45 parts by weight of the inorganic fibers (A), 1 to 45 parts by weight of the organic fibers (B), 10 to 93 parts by weight of the thermoplastic resin (C), and 1 to 20 parts by weight of the component (D), based on 100 parts by weight of a total of the inorganic fibers (A), the organic fibers (B), the thermoplastic resin (C), and the component (D),
• the inorganic fibers (A) and the organic fibers (B) are arranged almost parallel to an axial direction,
• lengths of the inorganic fibers (A) and the organic fibers (B) and a length of the fiber reinforced thermoplastic resin molding material are substantially equal to each other, and
• a length in a longer direction of the fiber reinforced thermoplastic resin molding material is 8 mm to 14 mm.

A fiber reinforced thermoplastic resin molding material comprising inorganic fibers (A), organic fibers (B), a thermoplastic resin (C), and a component (D) having a melt viscosity at 200° C. lower than that of the thermoplastic resin (C), composed of multiple different pellets, wherein

• the inorganic fibers (A) are carbon fibers,
• the fiber reinforced thermoplastic resin molding material comprises 5 to 45 parts by weight of the inorganic fibers (A), 1 to 45 parts by weight of the organic fibers (B), 10 to 93 parts by weight of the thermoplastic resin (C), and 1 to 20 parts by weight of the component (D), based on 100 parts by weight of a total of the inorganic fibers (A), the organic fibers (B), the thermoplastic resin (C), and the component (D),
• the multiple different pellets including a pellet (x) containing the inorganic fibers (A), the thermoplastic resin (C), and the component (D), and a pellet (y) containing the organic fibers (B), a thermoplastic resin (F), and a component (G),
• the inorganic fibers (A) are arranged almost parallel to an axial direction of the pellets (x), and the organic fibers (B) are arranged almost parallel to an axial direction of the pellets (y),
• lengths of the inorganic fibers (A) and the pellets (x) are substantially equal to each other, and lengths of the organic fibers (B) and the pellets (y) are substantially equal to each other, and
• lengths in a longer direction of the pellets (x) and the pellets (y) are 8 mm to 14 mm.