US 11,518,071 B2Granted
Rapid heat cycle molding
AssigneeArris Composites Inc.
InventorsErick Davidson, Ethan Escowitz, Arnaud Dyen, Christopher Bender
Life of this patent
Estimating the term…
Abstract
A method for rapid heat cycle compression molding comprises placing an assemblage of feed constituents in a mold, placing the mold between two hot platens of a hot press, heating the mold by pressing the two hot platens against the mold, placing the mold between two cold platens of a cold press, cooling the mold by pressing the two cold platens against the mold, and ejecting the part from the mold.
Claims15
A rapid heat cycle compression molding method for forming a composite part, the method comprising:
- a) positioning, at a first heating station, a mold containing of an assemblage of feed constituents, the first heating station having a first hot press including two platens, wherein the platens have a temperature that is above a processing temperature of a resin in the feed constituents;
- b) heating the mold by applying pressure to the mold by pressing the platens of the first hot press against the mold, wherein:
- (i) maintaining the pressure at a first pressure until a temperature of the mold is within about 25 degrees centigrade of the processing temperature of the resin;
- (ii) after the temperature of the mold is within about 25 degrees of the processing temperature, raising the pressure to a second pressure;
- and
- (iii) wherein the second pressure is within about 40 percent of the pressure required to fully consolidate the feed constituents, but less than the pressure required for full consolidation;
- c) transferring the mold to a first cooling station, the first cooling station having a first cold press including two platens, wherein the platens have a first temperature that is below the processing temperature of the resin;
- d) cooling the mold by applying pressure to the mold by pressing the platens of the first cold press against the mold, wherein the applied pressure is sufficient to fully consolidate the feed constituents, forming a composite part;
- and
- e) ejecting the composite part when the mold reaches an ejection temperature.
7 more elements
A rapid heat cycle compression molding method for forming a composite part, the method comprising:
- a) positioning, at a first heating station, a mold containing of an assemblage of feed constituents, the first heating station having a first hot press including two platens, wherein the platens have a temperature that is above a processing temperature of a resin in the feed constituents;
- b) heating the mold by applying pressure to the mold by pressing the platens of the first hot press against the mold, wherein the pressure is maintained at a first pressure and a temperature of the mold is raised to a first temperature that is within about 25 degrees centigrade of a processing temperature of the resin;
- c) when the temperature of the mold reaches the first temperature, transferring the mold to a second heating station having a second hot press including two platens;
- d) at the second heating station, raising the pressure to a second pressure and raising the temperature of the mold to a second temperature that is in excess of the processing temperature, wherein the second pressure is insufficient to fully consolidate the feed constituents, and wherein the platens have a temperature that is above a processing temperature of a resin in the feed constituents;
- e) transferring the mold to a first cooling station, the first cooling station having a first cold press including two platens, wherein the platens have a temperature that is below the processing temperature of the resin;
- f) cooling the mold by applying pressure to the mold by pressing the platens of the first cold press against the mold, wherein the applied pressure wherein the applied pressure is greater than the second pressure and is sufficient to fully consolidate the feed constituents, forming a composite part;
- and
- g) ejecting the composite part when the mold reaches an ejection temperature.
5 more elements
A rapid heat cycle compression molding method for forming a composite part, the method comprising:
- a) positioning, at a first heating station, a mold containing of an assemblage of feed constituents, the first heating station having a first hot press including two platens, wherein the platens have a temperature that is above a processing temperature of a resin in the feed constituents;
- b) heating the mold by applying pressure to the mold by pressing the platens of the first hot press against the mold, wherein the mold is heated to a first temperature that is at least as high as the processing temperature, and pressurized to a first pressure;
- c) transferring the mold to a first cooling station, the first cooling station having a first cold press including two platens, wherein the platens have a temperature that is below the processing temperature of the resin;
- d) cooling the mold at the first cooling station by pressing the platens of the first cold press against the mold, wherein the mold is cooled to a second temperature that is less than the processing temperature of the resin but greater than an ejection temperature of the mold, and wherein the pressure applied by pressing the platens is sufficient to fully consolidate the feed constituents;
- and
- e) after the mold is cooled to the second temperature, transferring the mold to a second cooling station having a second cold press, the second cold press having two platens that are maintained at a temperature that is less than the ejection temperature;
- f) cooling the mold to the ejection temperature by applying pressure;
- and
- g) ejecting the composite part when the mold reaches an ejection temperature.
6 more elements
A rapid heat cycle compression molding method for forming a composite part, the method comprising:
- a) positioning, at a first heating station, a mold containing of an assemblage of feed constituents, the first heating station having a first hot press including two platens, wherein the platens have a temperature that is above a processing temperature of a resin in the feed constituents;
- b) heating the mold by applying pressure to the mold by pressing the platens of the first hot press against the mold, wherein the mold is pressurized to a pressure that is insufficient to fully consolidate the feed constituents;
- c) transferring the mold to a first cooling station, the first cooling station having a first cold press including two platens, wherein the platens have a first temperature that is below the processing temperature of the resin;
- d) cooling the mold by applying pressure to the mold by pressing the platens of the first cold press against the mold, wherein the applied pressure is sufficient to fully consolidate the feed constituents, forming a composite part;
- and
- e) ejecting the composite part when the mold reaches an ejection temperature.
3 more elements