Process for the commercial production of high-quality catalyst materials

AssigneeGreyrock Technology, LLC

InventorsRobert Schuetzle, Dennis Schuetzle

Life of this patent

Estimating the term…

Loading patent…

Abstract

The present invention describes an improved process for the commercial scale production of high-quality catalyst materials. These improved processes allow for production of catalysts that have very consistent batch to batch property and performance variations. In addition these improved processes allow for minimal production losses (by dramatically reducing the production of fines or small materials as part of the production process). The improved process involves multiple steps and uses calcining ovens that allow for precisely control temperature increases where the catalyst is homogenously heated. The calcining gas is released into a separate heating chamber, which contains the recirculation fan and the heat source. Catalysts that may be produced using this improved process include but are not limited to catlaysts that promote CO hydrogenation, reforming catalysts, Fischer Tropsch Catalysts, Greyrock GreyCat™ catalysts, catalysts that homologate methanol, catalysts that promote hydrogenation of carbon compounds, and other catalysts used in industry.

Claims18

Dependent claims

A catalyst production process wherein catalyst materials are heated homogeneously in a calcining oven and in which the oven heating and gas flow rates are controlled, resulting in the production of catalysts that meet batch-to-batch chemical, physical and performance specifications with a high level of reproducibility, wherein the process comprises the steps of:

a. loading catalyst materials into a calcining oven;
b. wherein the calcining oven is connected to one or more separate reheating chambers, in which the calcining gas is heated using a thermostatically controlled heat source;
c. circulating the heated calcining gas from the reheating chambers into the calcining oven in which the gas is distributed over catalyst materials;
d. recirculating the calcining gas back into the reheating chambers at least 10 times;
e. increasing the oven temperature in increments ranging from about 0.5° F./min to about 10° F./min such that the temperature in any area of the oven does not vary more than about 25%;
f. maintaining the oven at a final calcining temperature for a period of time;
g. cooling the oven to ambient temperature at a controlled rate ranging from about 2° F./min to about 20° F./min.