Back to results
US 11,434,373 B2Granted
Formulations and products to replace single-use plastics and polystyrene with bio-benign materials such as agricultural wastes
AssigneeNutjobs
InventorsPaul Ray Kephart, John Warner, Samuel Ellman
Life of this patent
Estimating the term…
Abstract
The present invention provides methods for preparing the nut waste sheet composites from a nut waste component and one or more binders.
Claims15
A cured nut waste sheet composite, the cured nut waste sheet composite is prepared by the following steps:
- (a) providing a nut waste component selected from the group consisting of nut shells, nut hulls, and a combination of nut shells and nut hulls;
- (b) drying the nut waste component or adjusting the nut waste component to a pH of 5.0 to 8.0 then drying or sterilizing the nut waste component;
- (c) grinding the nut waste component to a size ranging from about greater than 500 μm to less than about 1000 μm;
- (d) contacting the nut waste component from step (c) with at least one or more binders selected from a group consisting of polyhydroxybutyrate (PHB), polyhydroxyalkanoate (PHA), polylactic acid (PLA), guayule, natural rubber latex, bentonite, an anionic starch, hyaluronic acid, triethyl citrate, and combinations thereof wherein the mixture in step (d) consists of about 5 wt% to 40 wt% of the nut waste component and 60.0 to 95.0 wt% of the binder;
- (e) heating the mixture to a temperature from about 80° C. to about 190° C. for about 5 minutes;
- (f) extruding the heated mixture into a sheet form;
- and
- (g) cooling the sheet wherein the cured nut waste sheet composite exhibits a thermal conductivity ranging from about 0.25 Wm-1K-1 to about 0.275 Wm-1K-1 at 23° C., a density from about 0.5 g/mL to about 0.75 g/mL, a Hardness from about 15 Konig to about 25 Konig, an Ultimate Tensile Strength from about 0.5 MPa to about 0.6 MPa, a Maximum Strain from about 263 to about 445, and an Elastic Modulus from about 0.053 MPa to about 0.057 MPa.
5 more elements
A cured nut waste sheet composite, the cured nut waste sheet composite is prepared by the following steps:
- (a) providing a nut waste component selected from the group consisting of nut shells, nut hulls, and a combination of nut shells and nut hulls;
- (b) drying the nut waste component or adjusting the nut waste component to a pH of 5.0 to 8.0 then drying or sterilizing the nut waste component;
- (c) grinding the nut waste component to a size ranging from about greater than 500 μm to less than about 1000 μm;
- (d) contacting the nut waste component from step (c) with of at least one or more binders selected from a group consisting of polyhydroxybutyrate (PHB), polyhydroxyalkanoate (PHA), polylactic acid (PLA), guayule, natural rubber latex, bentonite, an anionic starch, hyaluronic acid, triethyl citrate, and combinations thereof wherein the mixture in step (d) consists of about 40 wt% to 70 wt% of the nut waste component and 30.0 to 60.0 wt% of the binder;
- (e) heating the mixture to a temperature from about 80° C. to about 190° C. for about 5 minutes;
- (f) extruding the heated mixture into a sheet form;
- and
- (g) cooling the sheet wherein the cured nut waste sheet composite exhibits a thermal conductivity ranging from about 0.25 Wm-1K-1 to about 0.275 Wm-1K-1 at 23° C., a density from about 0.5 g/mL to about 0.75 g/mL, a Hardness from about 15 Konig to about 25 Konig, an Ultimate Tensile Strength from about 0.5 MPa to about 0.6 MPa, a Maximum Strain from about 263 to about 445, and an Elastic Modulus from about 0.053 MPa to about 0.057 MPa.
5 more elements
A cured nut waste sheet composite, the cured nut waste sheet composite is prepared by the following steps:
- (a) providing a nut waste component selected from the group consisting of nut shells, nut hulls, and a combination of nut shells and nut hulls;
- (b) drying the nut waste component or adjusting the nut waste component to a pH of 5.0 to 8.0 then drying or sterilizing the nut waste component;
- (c) grinding the nut waste component to a size ranging from about greater than 500 μm to less than about 1000 μm;
- (d) contacting of the nut waste component from step (c) with of at least one or more binders selected from a group consisting of polyhydroxybutyrate (PHB), polyhydroxyalkanoate (PHA), polylactic acid (PLA), guayule, natural rubber latex, bentonite, an anionic starch, hyaluronic acid, triethyl citrate, and combinations thereof wherein the mixture in step (d) consists of about 70 wt% to 95 wt% of the nut waste component and 5.0 to 30.0 wt% of the binder;
- (e) heating the mixture to a temperature from about 80° C. to about 190° C. for about 5 minutes;
- (f) extruding the heated mixture into a sheet form;
- and
- (g) cooling the sheet wherein the cured nut waste sheet composite exhibits a thermal conductivity ranging from about 25 Wm-1K-1 to about 0.275 Wm-1K-1, a density from about 0.5 g/mL to about 0.75 g/mL, a Hardness from about 15 Konig to about 25 Konig, an Ultimate Tensile Strength from about 0.5 MPa to about 0.6 MPa, a Maximum Strain from about 263 to about 445, and an Elastic Modulus from about 0.053 MPa to about 0.057 MPa.
5 more elements
Dependencies are inferred from the claim text.