US 11,377,714 B2Granted

Method for producing Ti-Al alloy

AssigneeKobe Steel, Ltd.

InventorsFumiaki Kudo, Daisuke Matsuwaka, Hitoshi Ishida, Tetsushi Deura

Life of this patent

Estimating the term…

Loading patent…

Abstract

A method includes the production of a primary ingot, the production of a secondary ingot, and the removal of a flux layer. A CaO—CaF2 flux in a content of 3-20 mass % and obtained by mixing 35-95 mass % of CaF2 with CaO is added to a Ti—Al alloy material including a total of at least 0.1 mass % of oxygen and at least 40 mass % of Al, and the resultant substance is melted by a melting method using a water-cooled copper container in an atmosphere having a pressure of 1.33 Pa or higher and held to produce the primary ingot. The primary ingot is continuously drawn downwards while being melted by a melting method using a bottomless water-cooled copper casting mould in an atmosphere having a pressure of 1.33 Pa or higher to produce the secondary ingot. The flux layer deposited on the surface of the secondary ingot is mechanically removed.

Claims4

Dependent claims

A method for producing a Ti—Al alloy, the method comprising:

(a) producing a primary ingot by melting and holding a melting raw material under an atmosphere of 1.33 Pa or more by a melting method using a water-cooled copper vessel to produce a primary ingot, wherein the melting raw material is prepared by adding a CaO—CaF2 flux to a Ti—Al alloy and contains from 3 to 20 mass % of the CaO—CaF2 flux relative to the Ti—Al alloy, the Ti—Al alloy is composed of a titanium material and an aluminum material and comprises 0.1 mass % or more of oxygen and 40 mass % or more of Al, and the CaO—CaF2 flux is prepared by mixing calcium fluoride with calcium oxide and comprises 35 to 95 mass % of the calcium fluoride:
(b) producing a secondary ingot by melting the primary ingot under an atmosphere of 1.33 Pa or more by a melting method using a bottomless water-cooled copper mold and continuously drawing the primary ingot downward to obtain the secondary ingot;
and
(c) mechanically removing a flux layer adhering to a surface of the secondary ingot.

1 more element

Dependencies are inferred from the claim text.