US 11,377,705 B2Granted
Grain-oriented electrical steel sheet
AssigneeNippon Steel Corporation
InventorsHiroyoshi Yashiki, Kenichi Murakami, Nobusato Morishige, Hirotoshi Tada, Yoshiaki Natori
Life of this patent
Estimating the term…
Abstract
A grain-oriented electrical steel sheet includes a steel layer and an insulation coating arranged in directly contact with the steel layer thereon. The steel layer includes, as a chemical composition, by mass %, 2.9 to 4.0% of Si, 2.0 to 4.0% of Mn, 0 to 0.20% of Sn, and 0 to 0.20% of Sb. In the steel layer, a silicon content and a manganese content expressed in mass % satisfy 1.2%≤Si−0.5×Mn≤2.0%, and a tin content and an antimony content expressed in mass % satisfy 0.005%≤Sn+Sb≤0.20%.
Claims5
A method of producing a grain-oriented electrical steel sheet,
- the method consisting of a casting process, a hot-rolling process, a cold-rolling process, a primary recrystallization annealing process, an annealing separator coating process, a secondary recrystallization annealing process, and an insulation coating formation process, wherein:
- in the casting process, a steel is cast so that the steel includes, as a chemical composition, by mass %,
- 0.0003 to 0.005% of C,
- 2.9 to 4.0% of Si,
- 2.0 to 4.0% of Mn,
- 0.003 to 0.018% of sol. Al,
- 0.001 to 0.01% of N,
- 0.005% or less of S,
- 0 to 0.20% of Sn,
- 0 to 0.20% of Sb, and
- a balance consisting of Fe and impurities,
- a silicon content and a manganese content expressed in mass % in the chemical composition satisfy 1.2% <Si - 0.5 x Mn <2.0%, and
- a tin content and an antimony content expressed in mass % in the chemical composition satisfy 0.005%≤Sn+Sb≤0.20%;
- in the primary recrystallization annealing process, a primary recrystallization annealing is conducted for the steel under conditions such that a heating rate in a temperature elevating stage is 100° C./second to 5000° C./second on average, an atmosphere in the temperature elevating stage is 10 to 100 vol % of H2 and H2+N2=100 vol %, a temperature in a holding stage is 800 to 1000° C., a time in the holding stage is 5 seconds to 10 minutes, an atmosphere in the holding stage is 10 to 100 vol % of H2, H2+N2=100 vol %, and a dew point is −10° C. or lower;
- in the annealing separator coating process, an annealing separator including an alumina as a main component is only applied on the steel;
- and
- in the secondary recrystallization annealing process, a secondary recrystallization annealing is conducted for the steel under conditions such that an atmosphere in a temperature elevating stage is 0 to 80 vol % of N2 and H2+N2=100 vol %, a dew point in a temperature range of 500° C. or higher in the temperature elevating stage is 0° C. or lower, a temperature in a holding stage is 850 to 1000° C., a time in the holding stage is 4 to 100 hours, an atmosphere in the holding stage is 0 to 80 vol % of N2, H2+N2=100 vol %, and a dew point is 0° C. or lower;
- and
- in the insulation coating formation process an insulation coating is formed on the steel after the secondary recrystallization annealing process.
16 more elements
A method of producing a grain-oriented electrical steel sheet,
- the method consisting of a casting process, a hot-rolling process, a cold-rolling process, a primary recrystallization annealing process, an annealing separator coating process, a secondary recrystallization annealing process, and an insulation coating formation process, wherein:
- in the casting process, a steel is cast so that the steel includes, as a chemical composition, by mass %,
- 0.0003 to 0.005% of C,
- 2.9 to 4.0% of Si,
- 2.0 to 4.0% of Mn,
- 0.003 to 0.018% of sol. Al,
- 0.001 to 0.01% of N,
- 0.005% or less of S,
- 0 to 0.20% of Sn,
- 0 to 0.20% of Sb, and
- a balance including Fe and impurities,
- a silicon content and a manganese content expressed in mass % in the chemical composition satisfy 1.2%≤Si−0.5×Mn≤2.0%, and
- a tin content and an antimony content expressed in mass % in the chemical composition satisfy 0.005%≤Sn+Sb≤0.20%;
- in the primary recrystallization annealing process, a primary recrystallization annealing is conducted for the steel under conditions such that a heating rate in a temperature elevating stage is 100° C./second to 5000° C./second on average, an atmosphere in the temperature elevating stage is 10 to 100 vol % of H2 and H2+N2=100 vol %, a temperature in a holding stage is 800 to 1000° C., a time in the holding stage is 5 seconds to 10 minutes, an atmosphere in the holding stage is 10 to 100 vol % of H2, H2+N2=100 vol %, and a dew point is −10° C. or lower;
- in the annealing separator coating process, an annealing separator including an alumina as a main component is only applied on the steel;
- and
- in the secondary recrystallization annealing process, a secondary recrystallization annealing is conducted for the steel under conditions such that an atmosphere in a temperature elevating stage is 0 to 80 vol % of N2 and H2+N2=100 vol %, a dew point in a temperature range of 500° C. or higher in the temperature elevating stage is 0° C. or lower, a temperature in a holding stage is 850 to 1000° C., a time in the holding stage is 4 to 100 hours, an atmosphere in the holding stage is 0 to 80 vol % of N2, H2+N2=100 vol %, and a dew point is 0° C. or lower;
- and
- in the insulation coating formation process an insulation coating is formed on the steel after the secondary recrystallization annealing process.
16 more elements
Dependencies are inferred from the claim text.