Back to results
US 11,370,713 B2Granted
Manufacturing method for ceramic composite material
AssigneeHUBLOT SA, Geneve
InventorMathias Buttet
Life of this patent
Estimating the term…
Abstract
Method for manufacturing a composite material combining a metal oxide or metalloid based matrix suited for allowing light to pass, and a mineral pigment dispersed in the matrix, the method comprising a step of mixing the mineral pigment in powder form with the matrix in powder form, and a step of sintering of the mixture under sufficient pressure such that the densification temperature of the matrix under said pressure is below the breakdown temperature of the mineral pigment, where the sintering temperature is greater than or equal to the densification temperature of the matrix and below the breakdown temperature of the mineral pigment.
Claims11
A method for manufacturing a product of watchmaking or jewelry making comprising a composite material, said composite material combining:
- a metal oxide or metalloid based matrix, where said matrix is suited for allowing light to pass after sintering and has densification temperatures which depend on the pressure to which said matrix is subject;
- a mineral pigment dispersed in the matrix, having a certain breakdown temperature beyond which said mineral pigment is broken down, wherein the mineral pigment is luminescent and comprises rare earth aluminates and/or rare earth silicates;
- where the densification temperatures of the matrix are greater than the breakdown temperature of the mineral pigment in at least one pressure range below 80 MPa;
- wherein manufacturing the composite material includes a sequence of transformation steps consisting:
- mixing the mineral pigment in powder form with the matrix in powder form;
- and
- sintering of said mixture of powders, in one single step, at a sintering temperature lower than 800° C. and under a pressure greater than or equal to 600 MPa sufficient in order that the densification temperature of the matrix under said pressure is below the breakdown temperature of the mineral pigment, where the sintering temperature is greater than or equal to the densification temperature of the matrix and below the breakdown temperature of the mineral pigment.
4 more elements
A method for manufacturing a product of watch making or jewelry making comprising a composite material, said composite material combining:
- a metal oxide or metalloid based matrix, in which said matrix is suited for allowing light to pass after sintering and has densification temperatures which depend on the pressure to which said matrix is subject;
- a mineral pigment dispersed in the matrix having a certain breakdown temperature beyond which said mineral pigment is broken down, in which the mineral pigment is luminescent and comprises rare earth aluminates and/or rare earth silicates, and the densification temperatures of the matrix are greater than the breakdown temperature of the mineral pigment in at least one pressure range below 80 MPa;
- wherein manufacturing the composite material includes a sequence of transformation steps consisting in:
- mixing the mineral pigment in powder form with the matrix in powder form;
- and
- sintering of said mixture of powders, in one single step, under pressure greater than or equal to 80 MPa sufficient in order that the densification temperature of the matrix under said pressure is below the breakdown temperature of the mineral pigment, in which the sintering temperature is greater than or equal to the densification temperature of the matrix and below the breakdown temperature of the mineral pigment.
3 more elements
A method for manufacturing a composite material, the composite material combining:
- a metal oxide or metalloid based matrix, where said matrix is suited for allowing light to pass after sintering and has densification temperatures which depend on the pressure to which said matrix is subject;
- a mineral pigment dispersed in the matrix, having a certain breakdown temperature beyond which said mineral pigment is broken down, wherein the mineral pigment is luminescent and comprises rare earth aluminates and/or rare earth silicates;
- where the densification temperatures of the matrix are greater than the breakdown temperature of the mineral pigment in at least one pressure range below 80 MPa;
- wherein manufacturing the composite material includes a sequence of transformation steps consisting in:
- mixing the mineral pigment in powder form with the matrix in powder form;
- and
- sintering of said mixture of powders, in one single step, at a sintering temperature lower than 800° C. and under a pressure greater than or equal to 600 MPa sufficient in order that the densification temperature of the matrix under said pressure is below the breakdown temperature of the mineral pigment, where the sintering temperature is greater than or equal to the densification temperature of the matrix and below the breakdown temperature of the mineral pigment.
4 more elements
A method for manufacturing a composite material, the composite material combining:
- a metal oxide or metalloid based matrix, where said matrix is suited for allowing light to pass after sintering and has densification temperatures which depend on the pressure to which said matrix is subject;
- a mineral pigment dispersed in the matrix, having a certain breakdown temperature beyond which said mineral pigment is broken down, wherein the mineral pigment is luminescent and comprises rare earth aluminates and/or rare earth silicates;
- where the densification temperatures of the matrix are greater than the breakdown temperature of the mineral pigment in at least one pressure range below 80 MPa;
- wherein manufacturing the composite material includes a sequence of transformation steps consisting in:
- mixing the mineral pigment in powder form with the matrix in powder form;
- and
- sintering of said mixture of powders, in one single step, under pressure greater than or equal to 80 MPa sufficient in order that the densification temperature of the matrix under said pressure is below the breakdown temperature of the mineral pigment, where the sintering temperature is greater than or equal to the densification temperature of the matrix and below the breakdown temperature of the mineral pigment.
4 more elements
Dependencies are inferred from the claim text.