Partially diffusion-alloyed steel powder

Abstract

Disclosed is a partially diffusion-alloyed steel powder having excellent fluidity, formability, and compressibility without containing Ni, Cr, and Si. A partially diffusion-alloyed steel powder having excellent fluidity, formability, and compressibility that includes an iron-based powder and Mo diffusionally adhered to a surface of the iron-based powder, in which Mo content is 0.2 mass % to 2.0 mass %, a weight-based median diameter D50 is 40 μm or more, and among particles contained in the partially diffusion-alloyed steel powder, those particles having an equivalent circular diameter of 50 μm to 200 μm have a number average of solidity of 0.70 to 0.86, the solidity being defined as (particle cross-sectional area/envelope-inside area).