Heat shrinkable film composition comprising polyethyleneterephtalate resin and polyester based copolymer, and heat shrinkable film

A heat shrinkable film, made by a method comprising:

• extruding a composition comprising:
• a polyethylene terephthalate (PET) resin having an inherent viscosity of 0.50 to 1.2dl/g;
• and
• a polyester based copolymer including a dicarboxylic acid-derived residue including a residue derived from an aromatic dicarboxylic acid;
• and
• a diol-derived residue including a residue derived from 4-(hydroxymethyl)cyclohexylmethyl 4′-(hydroxymethyl)cyclohexane carboxylate represented by the following Chemical Formula 1, a residue derived from 4,4-(oxybis(methylene)bis) cyclohexane methanol represented by the following Chemical Formula 2, and a residue derived from 1,4-cyclohexane dimethanol, to draw the extruded product,
• wherein the polyester based copolymer is prepared by reacting the dicarboxylic acid-derived residue and the diol-derived residue to perform an esterification reaction and a polycondensation reaction,
• wherein a total content of 4-(hydroxymethyl)cyclohexylmethyl 4′-(hydroxymethyl)cyclohexane carboxylate and the residue derived from 4,4-(oxybis(methylene)bis) cyclohexane methanol is 2 to 17 mol % of the entire diol,
• wherein the 4-(hydroxymethyl)cyclohexylmethyl 4′ (hydroxymethyl)cyclohexane carboxylate, the 4,4-(oxybis(methylene)bis) cyclohexane methanol, and the 1,4-cyclohexane dimethanol are present in an amount of 20 to 30 mol % relative to 100 mol % of the dicarboxylic acid, and
• wherein a temperature of a feeder of an extruder is lower than a temperature of a die, wherein the temperature of the die is between 270 and 275° C.