Soft polypropylene composition with improved properties

Soft heterophasic propylene copolymer composition, which comprises:

• (A) 50.0 to 99.0 wt % of a heterophasic polypropylene copolymer, said heterophasic propylene copolymer comprises:
• (a-1) a matrix (M) being a crystalline polypropylene homo- or copolymer and
• (a-2) elastomeric propylene copolymer (E) dispersed in said matrix (M),
• wherein the heterophasic polypropylene copolymer has;
• (i) a melt flow rate (MFR 230° C./2.16 kg, ISO1133) of 0.5 to 20.0 g/10 min,
• (ii) a xylene cold soluble (XCS) content determined according to ISO 16152 (25° C.) in the range of 15.0 to 30.0 wt %,
• (iii) a total ethylene or C4-C8 comonomer content in the range of 5.0 to 13.0 wt %,
• (iv) wherein the heterophasic polypropylene copolymer is free of phthalic acid esters or their decomposition products originating from a Ziegler-Nata catalyst, and
• (B) 1.0 to 50.0 wt % of a styrene-based elastomer (B) being a saturated block copolymer of styrene with ethylene and butylene or propylene, having a styrene content in the range of 5.0 to 22.0 wt % (measured with FTIR),
• the soft heterophasic propylene copolymer composition having a flexural modulus measured according to ISO 178 on injection moulded specimens of below 450 MPa.