Zirconia article with high alumina content, process of production and use thereof

Abstract

The invention relates to a porous zirconia article in particular for use in the dental or orthodontic field, the porous zirconia article comprising ZrO2: 80 to 87 wt. %, Y2O3: 3 to 5 wt. %, Al2O3: 10 to 14 wt. %, wt. % with respect to the weight of the porous zirconia article, the porous zirconia article being characterized by a BET surface from 15 to 100 m2/g. The invention also relates to a sintered zirconia article in particular for use in the dental or orthodontic field, the sintered zirconia article comprising ZrO2: 80 to 87 wt. %, Y2O3: 3 to 5 wt. %, Al2O3: 10 to 14 wt. %, wt. % with respect to the weight of the porous zirconia article, the sintered zirconia article being characterized by a corundum crystal phase content of 7 to 12 wt. % and a flexural strength of at least 2,000 MPa.