Silicon carbide fiber reinforced silicon carbide composite material

A method for producing a silicon carbide fiber reinforced silicon carbide composite material, comprising dispersing silicon carbide powder and powder of a substance having low reactivity with respect to silicon carbide in a dispersion medium to obtain a slurry;

• applying the slurry to a fiber structure of silicon carbide fibers to obtain a mixture;
• and then sintering the mixture under elevated pressure,
• wherein
• the substance is at least one member selected from the group consisting of graphite, BN, TaN, Cr2O3, ZrO2, HfO2, ZrC, NbC, HfC, TiB2, CrB2, Y2SiO5, Yb2SiO5, Yb2Si2O7, ErSiO5, LuSiO5, Sc2Si2O7, aluminosilicate, magnesium silicate, and barium-strontium aluminosilicate;
• the silicon carbide fiber reinforced silicon carbide composite material contains a multiphase matrix and the silicon carbide fibers disposed in the matrix, the matrix including a silicon carbide phase and a phase that contains the substance;
• the matrix has a structure in which the phase containing the substance is dispersed in the form of particles in the matrix;
• the silicon carbide fibers are silicon carbide long fibers;
• the silicon carbide phase consists of Si and C;
• and
• an interfacial phase is not present between the silicon carbon fibers and the matrix.

A method for producing a silicon carbide fiber reinforced silicon carbide composite material, comprising dispersing silicon carbide powder and powder of a substance having low reactivity with respect to silicon carbide in a dispersion medium to obtain a slurry;

• disposing bundled silicon carbide fibers in the slurry to obtain a mixture;
• and then sintering the mixture under elevated pressure,
• wherein
• the substance is at least one member selected from the group consisting of graphite, BN, TaN, Cr2O3, ZrO2, HfO2, ZrC, NbC, HfC, TiB2, CrB2, Y2SiO5, Yb2SiO5, Yb2Si2O7, ErSiO5, LuSiO5, Sc2Si2O7, aluminosilicate, magnesium silicate, and barium-strontium aluminosilicate;
• the silicon carbide fiber reinforced silicon carbide composite material contains a multiphase matrix and the silicon carbide fibers disposed in the matrix, the matrix including a silicon carbide phase and a phase that contains the substance;
• the matrix has a structure in which the phase containing the substance is dispersed in the form of particles in the matrix;
• the silicon carbide fibers are silicon carbide long fibers;
• the silicon carbide phase consists of Si and C;
• and
• an interfacial phase is not present between the silicon carbon fibers and the matrix.

A method for producing a silicon carbide fiber reinforced silicon carbide composite material, comprising drying a slurry containing silicon carbide powder and powder of a substance having low reactivity with respect to silicon carbide and molding into a sheet;

• forming a laminate by laminating thereon a fiber structure made of silicon carbide fibers or a layer in which bundled silicon carbide fibers are disposed;
• and then sintering the laminate under elevated pressure,
• wherein
• the substance is at least one member selected from the group consisting of graphite, BN, TaN, Cr2O3, ZrO2, HfO2, ZrC, NbC, HfC, TiB2, CrB2, Y2SiO5, Yb2SiO5, Yb2Si2O7, ErSiO5, LuSiO5, Sc2Si2O7, aluminosilicate, magnesium silicate, and barium-strontium aluminosilicate;
• the silicon carbide fiber reinforced silicon carbide composite material contains a multiphase matrix and the silicon carbide fibers disposed in the matrix, the matrix including a silicon carbide phase and a phase that contains the substance;
• the matrix has a structure in which the phase containing the substance is dispersed in the form of particles in the matrix;
• the silicon carbide fibers are silicon carbide long fibers;
• the silicon carbide phase consists of Si and C;
• and
• an interfacial phase is not present between the silicon carbon fibers and the matrix.

A method for producing a silicon carbide fiber reinforced silicon carbide composite material, comprising disposing a silicon carbide fiber aggregate in a reactor;

• supplying a mixed gas for vapor deposition containing a silicon carbide precursor gas for forming a silicon carbide phase and a second phase-forming precursor gas for forming a phase comprising a substance having low reactivity with respect to silicon carbide to the reactor;
• and heating the mixed gas for vapor deposition to a temperature at which both the silicon carbide precursor gas for forming the silicon carbide phase and the second phase-forming precursor gas undergo thermal decomposition, thereby vapor-depositing on the surfaces of the silicon carbide fibers the silicon carbide and the substance having low reactivity with respect to silicon carbide,
• wherein
• the substance is at least one member selected from the group consisting of graphite, BN, TaN, Cr2O3, ZrO2, HfO2, ZrC, NbC, HfC, TiB2, CrB2, Y2SiO5, Yb2SiO5, Yb2Si2O7, ErSiO5, LuSiO5, Sc2Si2O7, aluminosilicate, magnesium silicate, and barium-strontium aluminosilicate;
• the silicon carbide fiber reinforced silicon carbide composite material contains a multiphase matrix and the silicon carbide fibers disposed in the matrix, the matrix including the silicon carbide phase and the phase that contains the substance;
• the matrix has a structure in which the silicon carbide phase and the phase containing the substance are present at random in the form of non-uniform-shaped agglomerates in the matrix;
• the silicon carbide fibers are silicon carbide long fibers;
• the silicon carbide phase consists of Si and C;
• and
• an interfacial phase is not present between the silicon carbon fibers and the matrix.

A method for producing a silicon carbide fiber reinforced silicon carbide composite material, comprising dispersing a matrix-forming material containing powder containing a carbon component, Si powder, and powder of a substance having low reactivity with respect to silicon carbide in a dispersion medium to obtain a slurry;

• mixing the slurry with SiC fibers to obtain a mixture used for reaction sintering;
• and then heating the mixture to a temperature equal to or greater than the melting point of silicon,
• wherein
• the substance is at least one member selected from the group consisting of graphite, BN, TaN, Cr2O3, ZrO2, HfO2, ZrC, NbC, HfC, TiB2, CrB2, Y2SiO5, Yb2SiO5, Yb2Si2O7, ErSiO5, LuSiO5, Sc2Si2O7, aluminosilicate, magnesium silicate, and barium-strontium aluminosilicate;
• the silicon carbide fiber reinforced silicon carbide composite material contains a multiphase matrix and the silicon carbide fibers disposed in the matrix, the matrix including a silicon carbide phase and a phase that contains the substance;
• the matrix has a structure in which the phase containing the substance is dispersed in the form of particles in the matrix;
• the silicon carbide fibers are silicon carbide long fibers;
• the silicon carbide phase consists of Si and C;
• and
• an interfacial phase is not present between the silicon carbon fibers and the matrix.