Glass packaging ensuring container integrity
AssigneeCorning Incorporated
InventorsSteven Edward DeMartino, Robert Anthony Schaut
Life of this patent
Estimating the term…
Abstract
A strengthened glass container or vessel such as, but not limited to, vials for holding pharmaceutical products or vaccines in a hermetic and/or sterile state. The strengthened glass container undergoes a strengthening process that produces compression at the surface and tension within the container wall. The strengthening process is designed such that the tension within the wall is great enough to ensure catastrophic failure of the container, thus rendering the product unusable, should sterility be compromised by a through-wall crack. The tension is greater than a threshold central tension, above which catastrophic failure of the container is guaranteed, thus eliminating any potential for violation of pharmaceutical integrity.
Claims18
A method of making an aluminosilicate glass article having a first surface and a second surface separated by a thickness, the method comprising:
- forming a first region in at least one surface of the glass by ion-exchanging the glass, wherein the first region extends from at least one of the first surface or the second surface to a depth of layer in the glass, and wherein the first region is under a compressive stress and the thickness is from 0.9 mm to 1.2 mm;
- and
- forming a second region under a central tension of at least 15 MPa, the second region extending from the depth of layer, wherein the central tension is sufficient to allow self-propagation of a crack front from the first surface to the second surface and laterally across at least the first surface;
- wherein the glass article is a container adapted to hold a pharmaceutical product, a vaccine, a biologic, a foodstuff, or a solution.
A method of making a glass article comprising a glass and wherein the glass article has a first surface and a second surface separated by a thickness, the method comprising:
- forming a first region of the glass article, wherein forming the first region comprises applying a coating to at least one surface of the glass of the glass article, wherein the coating has a Young's modulus greater than the glass, wherein the first region extends from at least one of the first surface or the second surface to a depth of layer of the glass article, and wherein the first region comprises the coating and is under a compressive stress;
- and
- forming a second region under a central tension of at least 15 MPa, the second region extending from the depth of layer, wherein the central tension is sufficient to allow self-propagation of a crack front from the first surface to the second surface and laterally across at least the first surface.
A method of ensuring self-elimination of a vessel having an intended use, the method comprising:
- providing the vessel, the vessel comprising an ion-exchanged aluminosilicate glass, the vessel having a thickness of from 0.9 mm to 1.2 mm and a first surface and a second surface, wherein the glass has a first region under a compressive stress, the first region extending from at least one of the first surface or the second surface to a depth of layer in the glass, and a second region under a central tension of at least 15 MPa, the second region extending from the depth of layer, wherein the glass has a Young's modulus E and a Poisson's ratio ν, and (CT2/E)·(t−2DOL)·(1−ν)≥3.0 MPa·μm, where CT is the central tension, t is the thickness, and DOL is the depth of layer, wherein the central tension is greater than a threshold tensile stress that is sufficient to allow self-propagation of a crack front through the thickness from the first surface to the second surface, and wherein the self-propagation of the crack front from the first surface to the second surface renders the vessel unsuitable for its intended use.
Dependencies are inferred from the claim text.