Multi-pass plating process with intermediate rinse and dry
AssigneeTexas Instruments Incorporated
InventorsPeter John Holverson, Sudtida Lavangkul
Life of this patent
Estimating the term…
Abstract
A method includes electroplate depositing a first metal layer to a first thickness on a metal seed layer, rinsing the first metal layer with deionized water, and after the first rinse process, drying the wafer. The method also includes performing one or more additional electroplating processes that respectively deposit an additional metal layer to a second thickness over the first metal layer, performing an additional rinse process that rinses the additional metal layer with deionized water, and performing an additional drying processes that dries the wafer.
Claims17
A method of forming a metal layer, the method comprising:
- installing a wafer in an electroplating system;
- performing a first electroplating process in the electroplating system, wherein the first electroplating process deposits a first metal layer to a non-zero first thickness on a metal seed layer of the wafer;
- removing the wafer from the electroplating system after the first electroplating process;
- performing a first rinse process that rinses the first metal layer with deionized water;
- performing a first drying process that dries the wafer after the first rinse process;
- installing the wafer in the electroplating system after the first drying process;
- performing a second electroplating process in the electroplating system, wherein the second electroplating process deposits a second metal layer to a non-zero second thickness on the first metal layer;
- removing the wafer from the electroplating system after the second electroplating process;
- performing a second rinse process that rinses the second metal layer with deionized water;
- performing a second drying process that dries the wafer after the second rinse process, and
- after completing all the electroplating, rinsing, and drying processes of the metal layer without annealing the first and second metal layers, annealing the first and second metal layers.
8 more elements
A method of forming a metallization layer over a wafer, the method comprising:
- performing a first deposition process that deposits a dielectric layer on the wafer;
- forming an opening in the dielectric layer;
- performing a second deposition process that deposits a metal seed layer in the opening;
- performing a first electroplating process that deposits a first metal layer to a non-zero first thickness on the metal seed layer;
- after the first electroplating process, performing a first rinse process that rinses the first metal layer with deionized water;
- after the first rinse process, performing a first drying process that dries the wafer;
- after the first drying process:
- performing one or more additional electroplating processes that respectively deposit an additional metal layer to a non-zero second thickness over the first metal layer, until a total thickness of the first and additional metal layers exceeds a non-zero desired final thickness;
- after each of the additional electroplating processes, performing an additional rinse process that rinses the additional metal layer with deionized water;
- after each of the additional rinse processes, performing an additional drying process that dries the wafer;
- after a final one of the additional rinse processes, performing an annealing process that first anneals the first and additional metal layers;
- and
- after the annealing process, performing a chemical mechanical polishing (CMP) process that removes excess material from a top surface of the additional metal layers.
10 more elements
A method of fabricating an integrated circuit, the method comprising:
- performing a first deposition process that deposits a dielectric layer on a substrate;
- forming an opening in the dielectric layer;
- performing a second deposition process that deposits a metal seed layer in the opening and over the dielectric layer adjacent the opening;
- performing a first electroplating process that deposits a first metal layer to a non-zero first thickness on the metal seed layer both in the opening and over the dielectric layer adjacent the opening;
- after the first electroplating process, performing a first rinse process that rinses the first metal layer with deionized water;
- after the first rinse process, performing a first drying process that dries the wafer;
- after the first drying process:
- performing one or more additional electroplating processes that respectively deposit an additional metal layer to a non-zero second thickness over the first metal layer including over portions of the first metal layer in the opening and portions of the metal layer over the dielectric layer adjacent the opening;
- after each of the additional electroplating processes, performing an additional rinse process that rinses the additional metal layer with deionized water;
- after each of the additional rinse processes, performing an additional drying process that dries the wafer;
- after a final one of the additional rinse processes, performing a first anneal of the first and additional metal layers, wherein the first anneal is a first occurring anneal process since the deposition of the first metal layer;
- and
- after the annealing process, performing a chemical mechanical polishing (CMP) process that removes excess material from a top surface of the additional metal layers.