# US 11,027,485 B2 · Sheet-based additive manufacturing methods

> Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt

- Number: US 11,027,485 B2
- Document ID: US11027485B2
- Status: Granted
- Kind: B2
- Application number: 15/827,781
- Filed: 2017-11-30
- Published: 2019-05-30
- Granted: 2021-06-08
- Earliest claimed: 2017-11-30
- Assignees: The Boeing Company
- Applicants: The Boeing Company
- Inventors: Om Prakash; Nishant K. Sinha; Vijaykumar S. Ijeri
- Web page: https://patentgrep.com/patent/US11027485B2

## CPC

- B29C 64/147: using sheet material, e.g. laminated object manufacturing [LOM] or laminating sheet material precut to local cross sections of the 3D object
- B22F 12/41: characterised by the type, e.g. laser or electron beam
- B22F 12/45: Two or more
- B23K 26/21: by welding
- B23K 26/364: for making a groove or trench, e.g. for scribing a break initiation groove
- B23P 17/00: Metal-working operations, not covered by a single other subclass or another group in this subclass
- B29C 64/268: using laser beams; using electron beams [EB]
- B29C 64/282: of the same type, e.g. using different energy levels
- B29C 64/393: for controlling or regulating additive manufacturing processes
- B33Y 10/00: Processes of additive manufacturing
- B33Y 30/00: Apparatus for additive manufacturing; Details thereof or accessories therefor
- B33Y 50/02: for controlling or regulating additive manufacturing processes
- B22F 10/80: Data acquisition or data processing
- B22F 12/43: pulsed; frequency modulated
- B23P 2700/12: Laminated parts
- B29K 2101/12: Thermoplastic materials
- B29K 2105/256: {Sheets, plates, blanks or films}
- B29K 2995/0026: Transparent
- Y02P 10/25: Process efficiency
- B29C: SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING (making preforms B29B11/00; making laminated products by combining previously unconnected layers which become one product whose layers will remain together B32B37/00 - B32B41/00)
- B22F: WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER (making alloys by powder metallurgy C22C); APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
- B23K: SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
- B23P: METAL-WORKING NOT OTHERWISE PROVIDED FOR; COMBINED OPERATIONS; UNIVERSAL MACHINE TOOLS (arrangements for copying or controlling B23Q)
- B33Y: ADDITIVE MANUFACTURING, i.e. MANUFACTURING OF THREE-DIMENSIONAL [3D] OBJECTS BY ADDITIVE DEPOSITION, ADDITIVE AGGLOMERATION OR ADDITIVE LAYERING, e.g. BY 3D PRINTING, STEREOLITHOGRAPHY OR SELECTIVE LASER SINTERING
- B29K: INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR {MOULDS, } REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
- Y02P: CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS

## Abstract

A method of fabricating a part includes stacking sheets of fusible material to form a stack. The method also includes directing a laser beam through at least one sheet of the stack. The method also includes transferring energy from the laser beam to multiple locations on at least one interface between adjacent sheets of the stack, according to a predetermined pattern corresponding with a design of the part, to form corresponding multiple molten regions. The molten regions are conjoined together to form a fused portion of the adjacent sheets. The fused portion of the adjacent sheets defines the part.

## Claims

### Claim 1

A method of fabricating a part, the method comprising steps of:
forming a stack from at least two sheets of fusible material, the at least two sheets comprising a bottom sheet that comprises a bottom-sheet top surface, a bottom-sheet bottom surface, and a bottom-sheet thickness, separating the bottom-sheet top surface and the bottom-sheet bottom surface, and a top sheet that comprises a top-sheet top surface, a top-sheet bottom surface, and a top-sheet thickness, separating the top-sheet top surface and the top-sheet bottom surface, wherein the bottom sheet and the top sheet are stacked such that the top-sheet bottom surface and the bottom-sheet top surface form an interface between the top sheet and the bottom sheet;
directing a laser beam through the top-sheet top surface and through the top-sheet thickness such that the laser beam passes through the top-sheet top surface and through the top-sheet thickness without transferring energy to any portion of the top sheet so that no portion of the top sheet is melted; and
transferring the energy from the laser beam, directed through the top-sheet top surface and the top-sheet thickness, to multiple spaced-apart regions of the interface between the top sheet and the bottom sheet such that only a portion of the top-sheet thickness, abutting the multiple spaced-apart regions of the interface between the top sheet and the bottom sheet, and only a portion of the bottom-sheet thickness, abutting the multiple spaced-apart regions of the interface between the top sheet and the bottom sheet, are melted;
wherein melted portions of the top sheet of the stack and the bottom sheet of the stack define a fused portion of the of the stack and the fused portion of the stack defines at least a portion of the part.

### Claim 2 (depends on 1)

The method according to claim 1, further comprising:
selectively scoring adjacent sheets of the stack at a boundary between the fused portion of the stack and at least one unfused portion of the stack based on a preexisting computer-aided drafting model of the part; and
removing the at least one unfused portion of the stack from the fused portion of the stack.

### Claim 3 (depends on 1)

The method according to claim 1, wherein the fused portion of the stack is homogenous and forms a one-piece monolithic construction.

### Claim 4 (depends on 1)

The method according to claim 1, wherein the fusible material comprises a thermoplastic material.

### Claim 5 (depends on 4)

The method according to claim 4, wherein the thermoplastic material is optically transparent for at least one radiation wavelength.

### Claim 6 (depends on 1)

The method according to claim 1, wherein the step of transferring the energy from the laser beam to the multiple spaced-apart regions of the interface comprises a step of focusing the laser beam at the multiple spaced-apart regions.

### Claim 7 (depends on 6)

The method according to claim 6, wherein:
the at least two sheets further comprise a second top sheet that comprises a second-top-sheet top surface, a second-top-sheet bottom surface, and a second-top-sheet thickness, separating the second-top-sheet top surface and the second-top-sheet bottom surface, wherein the top sheet and the second top sheet are stacked such that the second-top-sheet bottom surface and the top-sheet top surface are in contact with each other and form a second interface between the second top sheet and the top sheet;
the method further comprises a step of directing the laser beam through the second-top-sheet top surface and through the second-top-sheet thickness such that the laser beam passes through the second-top-sheet top surface and through the second-top-sheet thickness without transferring the energy to any portion of the second top sheet so that no portion of the second top sheet is melted;
the method further comprises a step of transferring the energy from the laser beam, directed through the second-top-sheet top surface and the second-top-sheet thickness, to multiple second spaced-apart regions of the second interface between the second top sheet and the top sheet such that only a portion of the second-top-sheet thickness, abutting the multiple second spaced-apart regions of the second interface between the second top sheet and the top sheet, and only a portion of the top-sheet thickness, abutting the multiple second spaced-apart regions of the interface between the second top sheet and the top sheet, are melted; and
melted portions of the second top sheet of the stack and the top sheet of the stack further define the fused portion of the of the stack.

### Claim 8 (depends on 7)

The method according to claim 7, wherein the step of forming the stack comprises, after the laser beam is directed through the top-sheet top surface and through the top-sheet thickness and the energy from the laser beam is transferred to the multiple spaced-apart regions of the interface between the top sheet and the bottom sheet, comprises automatically feeding the second top sheet onto the top sheet using an actuator.

### Claim 9 (depends on 7)

The method according to claim 7, wherein:
the multiple spaced-apart regions of the interface are arranged in a first configuration;
the multiple second spaced-apart regions of the second interface are arranged in a second configuration; and
the first configuration is different than the second configuration.

### Claim 10 (depends on 6)

The method according to claim 6, wherein the step of focusing the laser beam at the multiple spaced-apart regions comprises at least one of moving the stack relative to the laser beam or adjusting a focus of the laser beam.

### Claim 11 (depends on 1)

The method according to claim 1, further comprising supplying a second energy to the stack concurrently with directing the laser beam through the top-sheet top surface and through the top-sheet thickness and with transferring the energy from the laser beam to the multiple spaced-apart regions of the interface.

### Claim 12 (depends on 11)

The method according to claim 11, wherein the second energy comprises at least one of thermal energy or ultrasonic energy.

### Claim 13 (depends on 1)

The method according to claim 1, further comprising positioning a sheet of metallic material between the bottom sheet and the top sheet, wherein:
the sheet of metallic material defines a portion of the interface between the top sheet and the bottom sheet; and
the sheet of metallic material comprises apertures each defining a respective one of the multiple spaced-apart regions of the interface between the top sheet and the bottom sheet.

### Claim 14 (depends on 1)

The method according to claim 1, wherein one of:
the bottom sheet is thicker than the top sheet; or
the top sheet is thicker than the bottom sheet.

### Claim 15 (depends on 1)

The method according to claim 1, wherein the fused portion has a three-dimensional compound shape.

### Claim 16 (depends on 1)

The method according to claim 1, further comprising, while directing the laser beam through the top-sheet top surface and through the top-sheet thickness and transferring the energy from the laser beam to the multiple spaced-apart regions of the interface between the top sheet and the bottom sheet:
directing a second laser beam through the top-sheet top surface; and
through the top-sheet thickness such that the second laser beam passes through the top-sheet top surface and through the top-sheet thickness without transferring the energy to any portion of the top sheet so that no portion of the top sheet is melted; and
transferring the energy from the second laser beam, directed through the top-sheet top surface and the top-sheet thickness, to multiple second spaced-apart regions of the interface between the top sheet and the bottom sheet such that only a portion of the top-sheet thickness, abutting the multiple second spaced-apart regions of the interface between the top sheet and the bottom sheet, and only a portion of the bottom-sheet thickness, abutting the multiple second spaced-apart regions of the interface between the top sheet and the bottom sheet, are melted;
wherein melted portions of the top sheet of the stack and the bottom sheet of the stack, melted by the energy from the second laser beam, define a second fused portion of the stack and the second fused portion of the stack defines at least a portion of a second part that is different from the part.

### Claim 17 (depends on 16)

The method according to claim 16, wherein the step of forming the stack comprises wrapping a continuous sheet of the fusible material about itself and a central core.

### Claim 18 (depends on 17)

The method according to claim 17, wherein the laser beam and the second laser beam are directed through the top-sheet top surface and through the top-sheet thickness in different directions that are transverse to a central axis of the central core.

### Claim 19 (depends on 1)

The method of claim 1, wherein:
the at least two sheets further comprise a second top sheet that comprises a second-top-sheet top surface, a second-top-sheet bottom surface, and a second-top-sheet thickness, separating the second-top-sheet top surface and the second-top-sheet bottom surface, wherein the top sheet and the second top sheet are stacked such that the second-top-sheet bottom surface and the top-sheet top surface are in contact with each other and form a second interface between the second top sheet and the top sheet; and
the step of directing the laser beam through the top-sheet top surface and through the top-sheet thickness further comprises directing the laser beam through the second-top-sheet top surface and through the second-top-sheet thickness such that the laser beam passes through the second-top-sheet top surface and through the second top-sheet thickness without transferring the energy to any portion of the second top sheet so that no portion of the second top sheet is melted.

### Claim 20 (depends on 1)

The method of claim 1, further comprising positioning a middle sheet between the bottom sheet and the top sheet, wherein:
the middle sheet defines a portion of the interface between the top sheet and the bottom sheet;
the middle sheet comprises a dye configured to absorb two photons of a first laser beam energy pulsed at a first rate and not absorb single photons of a second laser beam energy pulsed at a second rate;
the first rate is higher than the second rate;
the first laser beam energy is lower than the second laser beam energy; and
the laser beam is pulsed at the first rate and has photons of the first
laser beam energy, such that the energy from the laser beam is absorbed by the middle sheet, after being directed through the top-sheet top surface and through the top-sheet thickness, and transferred from the middle sheet to the bottom sheet and the top sheet to melt only the portion of the top-sheet thickness, abutting the multiple spaced-apart regions of the interface between the top sheet and the bottom sheet, and melt only the portion of the bottom-sheet thickness, abutting the multiple spaced-apart regions of the interface between the top sheet and the bottom sheet.

### Claim 21 (depends on 2)

The method according to claim 2, wherein:
the laser beam is generated by a formation laser; and
the adjacent sheets of the stack are scored at the boundary between the fused portion of the stack and the at least one unfused portion of the stack by a second laser beam generated by a separation laser that is different than the formation laser.

### Claim 22 (depends on 2)

The method according to claim 2, wherein:
the laser beam is generated by a formation laser; and
the adjacent sheets of the stack are scored at the boundary between the fused portion of the stack and the at least one unfused portion of the stack by a second laser beam generated by the formation laser.