Thermoplastic polyurethane materials for forming medical devices
AssigneeBecton, Dickinson and Company
InventorsMing Zhou, Theresa Hermel-Davidock
Life of this patent
Estimating the term…
Abstract
Principles and embodiments of the present invention relate generally to thermoplastic polyurethane materials having controlled and improved stiffness and/or flexibility, and methods to prepare them. The thermoplastic polyurethanes described herein having superior stiffness and softening properties may be fabricated into film, tubing, and other forms of medical devices. The thermoplastic polyurethanes comprise: an aromatic diisocyanate excluding non-aromatic diisocyanates; at least one polyglycol; and a chain extender comprising at least one side-chain branching diol and excluding linear diols.
Claims5
A melt-processable thermoplastic polyurethane comprising the reaction product of the following ingredients:
- 46 to 49% by weight of an aromatic diisocyanate that is 4,4′-diphenylmethane diisocyanate;
- 14 to 28% by weight of a first polytetramethylene ether glycol (PTMEG) having a first nominal molecular weight in the range of 250 to less than 1000 daltons;
- 15 to 25% by weight of a second PTMEG having a second nominal molecular weight in the range of 1000 to 2900 daltons;
- and
- 12 to 18% by weight of a chain extender consisting of:
- 2,2-dimethyl-1,3-propanediol;
- with the proviso that amounts of the aromatic diisocyanate, the first and second PTMEGs, and the chain extender add to 100%;
- wherein the hard segment content is in a range of 60 to 65% and when the thermoplastic polyurethane is melt-processed to form 18-gauge tubing, the thermoplastic polyurethane is effective to exhibit a degree of softening of 81.5% going from an ambient condition of 23° C. and 50% relative humidity for 24 hours to a simulated body environment of 37° C. in saline solution for 24 hours.