Multiple layer panels having reduced levels of edge defects
AssigneeSolutia Inc.
InventorsJun Lu, Kok Leong William Aw, John Joseph D'Errico
Life of this patent
Estimating the term…
Abstract
A process for producing a multilayer glass laminate panel having two glass sheets with a poly(vinyl butyral) interlayer sandwiched therebetween, the process comprising the steps of: providing two glass sheets; providing a poly(vinyl butyral) interlayer, and inserting the interlayer between the two glass sheets to produce a laminate; removing air from the produced laminate; applying heat and pressure to the laminate for a hold time, wherein the laminate is free of bubbles at the edges of the laminate. The multilayer glass laminate panel has improved optical properties, and specifically reduced levels of edge defects, such as edge bubbles in the laminate.
Claims7
A process for producing a multilayer glass laminate panel comprising two glass sheets with a poly(vinyl butyral) interlayer sandwiched therebetween, the process comprising the steps of:
- providing two glass sheets;
- providing a poly(vinyl butyral) interlayer, wherein said interlayer is tri-layer having two rigid skin layers and a soft core layer, where said skin layers have a glass transition temperature of from 30° C. or greater and said core layer has a glass transition temperature of less than about 4° C. and inserting the interlayer between the two glass sheets to produce a laminate;
- removing air from the produced laminate;
- and
- autoclaving the laminate for a hold time, wherein the heat is at a temperature in the range of from about 110° C. to about 155° C., the pressure is from 4.1 to about 6.9 bars, and the hold time is in a range of from about 10 minutes to about 60 minutes;
- wherein the glass laminate panel is free of bubbles at the edges of the laminate panel;
- and wherein the pummel adhesion rating ranges from 3 to 7.
A process for producing a multilayer glass laminate panel comprising two glass sheets with a poly(vinyl butyral) interlayer sandwiched therebetween, the process comprising the steps of:
- providing two glass sheets;
- providing a multilayer poly(vinyl butyral) interlayer wherein said interlayer is tri-layer having two rigid skin layers and a soft core layer, where said skin layers have a glass transition temperature of from 30° C. or greater and said core layer has a glass transition temperature of less than about 4° C., and inserting the interlayer between the two glass sheets to produce a laminate;
- removing air from the produced laminate;
- and
- autoclaving the laminate for a hold time, wherein the heat is at a temperature in the range of from about 110° C. to about 155° C., the pressure is in a range of from about 4.1 to about 6.9 bars, and the hold time is in a range of from about 10 minutes to about 60 minutes and wherein the glass laminate panel is free of bubbles at the edges of the laminate panel and wherein the pummel adhesion rating ranges from 3 to 5.
Dependencies are inferred from the claim text.