Deacidifying and reinforcing agent for cellulose acetate film
AssigneeShaanxi Normal University
InventorsZhihui Jia, Yuhu Li
Life of this patent
Estimating the term…
Abstract
A method for preparing a deacidifying and reinforcing agent for a cellulose acetate film includes steps of: ultrasonically dispersing a nanometer alkaline oxide into an ethyl cellulose n-butanol solution, so as to form a nanometer alkaline oxide suspension, then adding a mixture of E51 EPOXY RESIN and a curing agent thereof; wherein the nanometer alkaline oxide is a nanometer magnesium oxide, a nanometer cerium oxide, a nanometer magnesium hydroxide, a nanometer potassium carbonate, a nanometer calcium hydroxide or a nanometer barium hydroxide. A method for using the deacidifying and reinforcing agent includes steps of: evenly applying the deacidifying and reinforcing agent on a surface of a cellulose acetate film.
Claims8
A deacidifying and reinforcing agent for a cellulose acetate ester film, comprising:
- an ethyl cellulose alcohol solution;
- a nanometer alkaline oxide;
- and
- a mixture of epoxy resin and a curing agent thereof, which are mixed according to a mass fraction of 100:(0.8-1.5):(2-5);
- wherein in the mixture of the epoxy resin and the curing agent thereof, a mass fraction is 1:1.
A method for preparing a deacidifying and reinforcing agent for a cellulose acetate ester film, comprising steps of:
- 1) selecting an ethyl cellulose alcohol solution, a nanometer alkaline oxide, and a mixture of epoxy resin and a curing agent thereof, according to a mass fraction of 100:(0.8-1.5):(2-5);
- wherein in the mixture of the epoxy resin and the curing agent thereof, a mass fraction is 1:1;
- and
- 2) ultrasonically dispersing the nanometer alkaline oxide into the ethyl cellulose alcohol solution, so as to form a nanometer alkaline oxide suspension, then adding the mixture of the epoxy resin and the curing agent thereof into the nanometer alkaline oxide suspension and thoroughly mixing, so as to obtained the deacidifying and reinforcing agent for the cellulose acetate ester film.
Dependencies are inferred from the claim text.