Full-view-field quantitative statistical distribution characterization method of precipitate particles in metal material

A full-view-field quantitative statistical distribution characterization method of precipitate particles in a metal material, comprising the following steps:

• (1) electrolytic polishing and corrosion of a metallic material specimen:
• first, performing electrolytic polishing on the metallic material specimen after mechanical polishing is performed, so that a surface of the metallic material specimen is bright, clean and smooth;
• and
• then, performing electrolytic corrosion on the metallic material specimen after electrolytic polishing is performed, so that precipitate particles stand out from the surface of the metallic material specimen;
• (2) automatic collection of characteristic images of microstructures:
• positioning and marking a characteristic region of the surface of the metallic material specimen on which electrolytic corrosion is performed, performing automatic collection of characteristic images of full-view-field microstructures on a marked region using a full-automatic metallographic microscope, to obtain a plurality of characteristic images of full-view-field microstructures containing the precipitate particles combined with image synthesis;
• and meanwhile, recording three-dimensional coordinates of the precipitate particles in different focusing positions, to obtain a plurality of 3D morphology distribution diagrams of the precipitate particles;
• (3) automatic stitching and fusion of the characteristic images of full-view-field microstructures:
• for the plurality of clear characteristic images of full-view-field microstructures containing the precipitate particles obtained in the step (2), acquiring mutual information for searching metallographic characteristic images through entropies and joint entropy of any two characteristic images of microstructures of different view fields using a mutual information-based image registration algorithm, and determining a position and size of adjacent overlap regions, so that automatic identification and stitching of the overlap regions of the characteristic images of full-view-field microstructures are realized;
• and performing mathematical processing on edge grayscales of the stitched characteristic images of full-view-field microstructures, so that the grayscales are homogenized and fused, and a characteristic image of the full-view-field microstructure in a large-range microstructure containing a plurality of the precipitate particles is obtained;
• (4) automatic identification and segmentation of the precipitate particles:
• performing a process of noise elimination, segmentation, binarization, hole filling, fragment removal on the characteristic image of the full-view-field microstructure in a large range containing the plurality of precipitate particles obtained in the step (3), to obtain a preprocessed image;
• performing Euclidean distance transformation on the preprocessed image;
• and performing segmentation on the preprocessed image on which Euclidean distance transformation is performed with a watershed by using a watershed algorithm, to obtain a segmented characteristic image of the full-view-field microstructure;
• (5) quantitative distribution characterization of large-range full-view-field precipitate particles:
• performing statistical distribution analysis of the precipitate particles on the 3D morphology distribution diagrams of the precipitate particles obtained in the step (2) and on the segmented characteristic image of the full-view-field microstructure obtained in the step (4), to obtain the position, morphology, area and equivalent circle diameter of each precipitate particle in the large-range full view field and quantitative statistical distribution data of particle number distribution and area fraction distribution within different particle size ranges,
• in the step (1), the metallic material specimen after mechanical polishing is performed is taken as an anode, and a stainless steel sheet is taken as a cathode;
• in the process of electrolytic polishing, an electrolytic solution is a mixed solution of inorganic acid and methanol, wherein a volume ratio of inorganic acid to methanol is 1:3 to 1:4, a voltage is 20V-40V, and an electrolytic duration is 10 s-100 s;
• and
• in the process of electrolytic corrosion, an electrolytic solution is a mixed solution of inorganic acid and chromic trioxide, wherein a voltage is 0.1V-5V, an electrolytic duration is 1 s-30 s, and an electrolytic temperature is 0° C.-25° C., wherein the mixed solution of inorganic acid and chromic trioxide is prepared by adding 10 g-20 g of chromic trioxide into 150 mL-200 mL of inorganic acid solution.