Sliding member, clutch plate, and manufacturing methods for the same
AssigneeJtekt Corporation
InventorsKazutaka Matsukawa, Hiroyuki Ando, Yasunari Saito, Hideyuki Saito, Kazuhiro Fukushima, Tomoyuki Nanba
Life of this patent
Estimating the term…
Abstract
In a manufacturing method for a sliding member, a nitrogen diffusion layer, a nitrogen compound layer, and an oxidation layer are formed by executing a first step of cooling a workpiece formed of a steel material after heating the workpiece in an atmosphere containing ammonia at 570 to 660° C., a second step of performing, subsequently to the first step, tempering while pressurizing a front surface side of the workpiece, and a third step of performing, subsequently to the second step, steam treatment of heating the workpiece in a steam atmosphere.
Claims5
A manufacturing method for a pilot clutch plate, comprising:
- a first step of heating a base material portion formed of a steel material in an atmosphere containing ammonia at 570 to 660° C. and then cooling the base material portion, to form a nitrogen diffusion layer on a front surface of the base material portion;
- a second step, performed subsequently to the first step, of tempering the base material portion while pressurizing the front surface of the base material portion having the nitrogen diffusion layer thereon, to form a nitrogen compound layer on a front surface of the nitrogen diffusion layer;
- and
- a third step, performed subsequently to the second step, of performing steam treatment on the base material portion having the nitrogen diffusion layer and the nitrogen compound layer thereon, to form an oxidation layer on a front surface of the nitrogen compound layer by sequential steps of:
- heating the base material portion having the nitrogen diffusion layer and the nitrogen compound layer thereon to an elevated treatment temperature in a nitrogen atmosphere, and maintaining the base material portion at the elevated treatment temperature in the nitrogen atmosphere for a time sufficient to preheat the workpiece, and
- maintaining the preheated workpiece at the elevated treatment temperature in a steam atmosphere for a time sufficient to form the oxidation layer on the front surface of the nitrogen compound layer.
Dependencies are inferred from the claim text.