Vinyl chloride resin composition, vinyl chloride resin molded product, and laminate

A vinyl chloride resin molded product obtained through molding of a vinyl chloride resin composition comprising:

• a vinyl chloride resin (a);
• a plasticizer (b);
• an amide compound (c) indicated by formula (1), shown below,
• R1(NR2COR3)n (1)
• where, in formula (1), n is an integer of not less than 2 and not more than 6, R1 is a hydrocarbon group having a carbon number of from 1 to 8, R2 is hydrogen or a hydrocarbon group having a carbon number of from 1 to 2, and R3 is an unsaturated hydrocarbon group having a carbon number of from 11 to 23 and including at least one carbon-carbon unsaturated bond;
• and
• an amide compound (d) indicated by formula (2), shown below,
• R4(NR5COR6)n (2)
• where, in formula (2), n is an integer of not less than 2 and not more than 6, R4 is a hydrocarbon group having a carbon number of from 1 to 8, R5 is hydrogen or a hydrocarbon group having a carbon number of from 1 or 2, and R6 is a saturated hydrocarbon group having a carbon number of from 11 to 23;
• wherein the amide compound (d) has a higher melting point than the amide compound (c) such that a mixture of the amide compounds (c) and (d) has a single melting point of not lower than 124° C. and not higher than 142° C.,
• wherein content of the plasticizer (b) is not less than 10 parts by mass and not more than 200 parts by mass per 100 parts by mass of the vinyl chloride resin (a),
• content of the compound (c) is not less than 0.04 parts by mass and not more than 2.0 parts by mass per 100 parts by mass of the vinyl chloride resin (a),
• content of the amide compound (d) is not less than 0.04 parts by mass and not more than 0.4 parts by mass per 100 parts by mass of the vinyl chloride resin (a),
• wherein the vinyl chloride resin molded product shows no change in surface state after 500 hours storage at a temperature of 120° C.