Biomolecule-functionalised PVC and production method thereof
AssigneeUniversidad De Chile
InventorsMarcela Urzúa Acevedo, Carolina Sandoval Rocuant, Mehrdad Yazdani-Pedram Zobeiri, Rafael Martinez Figueroa
Life of this patent
Estimating the term…
Abstract
The present invention relates to the medical industry. In particular, it is related to a polyvinyl chloride polymer (PVC) functionalized for medical use, which is flexible and compatible with blood. Specifically, this invention is related to a biomolecule-functionalized PVC and its production method, in order to produce a flexible and blood-compatible polymer for medical use.
Claims8
A method for producing a functionalized polyvinyl chloride (PVC), CHARACTERIZED in that it comprises the following steps:
- i. mixing a PVC of molecular weight of less than 200,000 g/mol with one or more amino acids (Aa) selected from the group of amino acids having hydropathic index between −3.5 and 1.8 and a catalyst selected from the group of alkaline carbonates having a molar ratio selected from 1:1:1 to 2:2:1 (PVC:amino acid:catalyst), in a dissolution solvent and under inert atmosphere;
- ii. stirring the mixture at 1,000 rpm, keeping under a constant temperature between 50° C. and 120° C. for between 20 and 120 minutes;
- iii. precipitating the polymer in a precipitation solvent;
- iv. centrifuging between 5,000 and 12,000 rpm for 10 to 60 minutes at 25° C. temperature;
- v. purifying the functionalized polymer by dissolving in a dissolution solvent and precipitating in a precipitation solvent.
A functionalized vinyl polyvinyl chloride (PVC) polymer CHARACTERIZED in that it comprises molecular weights of less than 200,000 g/mol;
- wherein FT-IR spectrum of each functionalized PVC shows the absorption band corresponding to the C═C stretch at 1,630 cm−1, the absorption band corresponding to the C═O stretch at 1,734 cm−1 and a wide absorption band at 3,340 cm−1 corresponding to the O—H stretch vibration;
- wherein the absorption band corresponding to the N—H stretch is coupled with the band associated with the O—H group and wherein the absorption band corresponding to the C—Cl stretch is observed at 685;
- wherein its 1H NMR spectrum shows an intense signal at 5 ppm, which corresponds to olefin protons (—CH═CH—) present in a large part of the polymer chain, a signal at 2.5 ppm corresponding to the proton of the amino group (—NH—), a signal at 3.3 ppm that corresponds to a coupling of the signals associated with the methine proton linked to the amino acid residue (CH—N) and the methine proton linked to the chlorine atom (CH—Cl), a signal at 4, 2 ppm associated with the methylen proton of the amino acid residue;
- wherein its 13C NMR spectrum shows two signals at 40 and 70 ppm corresponding to the presence of methine and methylene carbons, and a signal at 135 ppm corresponding to the olefin carbons (CH═CH) present in the polymer chain.
Dependencies are inferred from the claim text.