Method for preparing transparent free-standing titanium dioxide nanotube array film

A method for preparing a transparent free-standing titanium dioxide nanotube array film, comprising the following steps:

• (1) using a titanium foil subjected to pre-treatment as an anode and an inert electrode as a cathode, placing the cathode and the anode into an organic electrolyte, applying a voltage, and carrying out anode oxidation at room temperature;
• and upon completion of the oxidation, washing the anode with deionized water, naturally drying to obtain a titanium foil with a titanium dioxide nanotube array film grown on a surface thereof;
• the titanium foil has a thickness of 0.01-0.02 mm, and the titanium foil has a purity of 99.0-99.9%;
• the pre-treatment comprises ultrasonic cleaning the titanium foil sequentially in acetone, ethanol and deionized water for 10 to 20 minutes, and naturally drying the titanium foil;
• and
• (2) carrying out high temperature annealing for the titanium foil with the titanium dioxide nanotube array film grown on the surface thereof, and cooling to room temperature upon completion of the high temperature annealing, such that the titanium dioxide nanotube array film on the surface of the titanium foil falls off and the transparent free-standing titanium dioxide nanotube array film in anatase phase is obtained,
• wherein in step (2), the high temperature annealing is carried out in an air atmosphere by increasing the temperature to 450° C. at a heating rate of 10° C./min and maintaining the temperature for 2-6 hours,
• wherein in step (2), a temperature raising process of the high temperature annealing comprises:
• raising the temperature to 100° C. at the heating rate of 10° C./min, and maintaining the temperature at 100° C. for 10 minutes;
• then raising the temperature to 200° C. at the heating rate of 10° C./min, and maintaining the temperature at 200° C. for 10 minutes;
• and raising the temperature to 300° C. and 400° C. at the heating rate of 10° C./min, and likewise maintaining the temperature at 300° C. and 400° C. for 10 minutes respectively, until the temperature reaches 450° C.