# US 10,865,257 B2 · Production methods for aqueous emulsion, fine powder and stretched porous body of modified polytetrafluoroethylene

> Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt

- Number: US 10,865,257 B2
- Document ID: US10865257B2
- Status: Granted
- Kind: B2
- Application number: 15/875,427
- Filed: 2018-01-19
- Published: 2018-05-24
- Granted: 2020-12-15
- Earliest claimed: 2015-08-19
- Assignees: AGC Inc.
- Applicants: AGC Inc.
- Inventors: Shinya Higuchi; Hiroki Nagai; Shigeki Kobayashi
- Web page: https://patentgrep.com/patent/US10865257B2

## CPC

- C08F 2/26: anionic
- B29C 48/288: {in solid form, e.g. powder or granules}
- C08F 6/22: Coagulation
- C08F 14/26: Tetrafluoroethene
- C08F 214/26: Tetrafluoroethene
- C08J 3/16: by coagulating dispersions {(C08J3/122 takes precedence)}
- B29C 48/0018: {combined with shaping by orienting, stretching or shrinking, e.g. film blowing (B29C48/0017 takes precedence)}
- B29C 48/02: Small extruding apparatus, e.g. handheld, toy or laboratory extruders
- B29C 48/08: flexible, e.g. films
- B29C 48/92: Measuring, controlling or regulating
- B29C 55/005: {characterised by the choice of materials}
- B29C 2948/92019: Pressure
- B29K 2027/18: PTFE, i.e. polytetrafluoroethylene {, e.g. ePTFE, i.e. expanded polytetrafluoroethylene}
- B29K 2105/04: cellular or porous
- C08J 2427/18: Homopolymers or copolymers of tetrafluoroethylene
- C08F: MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- B29C: SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING (making preforms B29B11/00; making laminated products by combining previously unconnected layers which become one product whose layers will remain together B32B37/00 - B32B41/00)
- C08J: WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H (working, e.g. shaping, of plastics B29)
- B29K: INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR {MOULDS, } REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS

## Abstract

To provide a production method for an aqueous emulsion of modified polytetrafluoroethylene which is environmentally friendly and which is suitable for producing a stretched porous body having excellent breaking strength. A production method for an aqueous emulsion of modified polytetrafluoroethylene, which is a method to obtain an aqueous emulsion of modified polytetrafluoroethylene particles having an average primary particle diameter of from 0.10 to 0.30 μm, by subjecting tetrafluoroethylene and a perfluoroalkyl ethylene to emulsion polymerization in an aqueous medium, using a polymerization initiator, in the presence of a fluorinated anionic surfactant having a LogPOW of from 2.4 to 3.4, wherein the amount of the perfluoroalkyl ethylene to be used, is from 120 to 3,000 ppm to the final production amount of the modified polytetrafluoroethylene; at the initiation of the emulsion polymerization, the entire amount of the perfluoroalkyl ethylene is permitted to be present, and, as the polymerization initiator, either one or both of a combination of a bromate and a bisulfite or sulfite, and a combination of a permanganate and oxalic acid, are used.

## Claims

### Claim 1

A production method for an aqueous emulsion of modified polytetrafluoroethylene, which is a method to obtain an aqueous emulsion of non-melt-moldable modified polytetrafluoroethylene particles having an average primary particle diameter of from 0.10 to 0.30 μm, by subjecting tetrafluoroethylene and a perfluoroalkyl ethylene represented by the following formula (1) to emulsion polymerization in an aqueous medium, in a polymerization reactor using a polymerization initiator, in the presence of a fluorinated anionic surfactant having a LogPOW of from 2.4 to 3.4,
wherein
an amount of the perfluoroalkyl ethylene to be used, is from 120 to 3,000 ppm (by mass) to the final production amount of the modified polytetrafluoroethylene,
the entire amount of the perfluoroalkyl ethylene is charged to the polymerizarion reactor such that at the initiation of the emulsion polymerization, the entire amount of the perfluoroalkyl ethylene is present,
an amount of the fluorinated anionic surfactant present in the emulsion polymerization is from 1.09 to 2 mass % based on the final production amount of the modified polytetrafluoroethylene,
and
as the polymerization initiator, either one or both of a combination of a bromate and a bisulfite or sulfite, and a combination of a permanganate and oxalic acid, are used:
CH2═CH—Rf (1)
wherein Rf is a C1-6 perfluoroalkyl group.

### Claim 2 (depends on 1)

The production method for an aqueous emulsion of modified polytetrafluoroethylene according to claim 1, wherein the fluorinated anionic surfactant is a fluorinated surfactant having 6 or 7 carbon atoms, 0 or 1 hydrogen atom, 0 or from 1 to 4 etheric oxygen atoms, a group represented by —COOA, wherein A is H, NH4 or an alkali metal atom and the rest of atoms being fluorine atoms.

### Claim 3 (depends on 1)

The production method for an aqueous emulsion of modified polytetrafluoroethylene according to claim 1, wherein the perfluoroalkyl ethylene is CH2═CH(CF2)2F, CH2═CH(CF2)4F or CH2═CH(CF2)6F.

### Claim 4 (depends on 3)

The production method for an aqueous emulsion of modified polytetrafluoroethylene according to claim 3, wherein the perfluoroalkyl ethylene is CH2═CH(CF2)4F or CH2═CH(CF2)6F.

### Claim 5 (depends on 1)

A production method for a fine powder of modified polytetrafluoroethylene, which comprises producing an aqueous emulsion of modified polytetrafluoroethylene particles by the method as defined in claim 1, coagulating the obtained aqueous emulsion, and drying the obtained wet state fine powder of modified polytetrafluoroethylene, to obtain a powder having a standard specific gravity of from 2.130 to 2.145.

### Claim 6 (depends on 5)

The production method for a fine powder of modified polytetrafluoroethylene according to claim 5, wherein the drying of the wet state fine powder of modified polytetrafluoroethylene is carried out in an atmosphere containing ammonia.

### Claim 7 (depends on 5)

The production method for a fine powder of modified polytetrafluoroethylene according to claim 5, wherein the standard specific gravity is from 2.135 to 2.142.

### Claim 8 (depends on 5)

The production method for a fine powder of modified polytetrafluoroethylene according to claim 5, wherein the extrusion pressure in the following extrusion test of the fine powder of modified polytetrafluoroethylene is from 19 to 25 MPa:
Extrusion test: 100 g of the fine powder of modified polytetrafluoroethylene left to stand for at least 2 hours at room temperature is put into a glass bottle having an internal capacity of 500 mL, and 21.7 g of a lubricating oil (Isopar H (registered trademark), manufactured by Exxon) is added and mixed for 3 minutes to obtain a mixture; and the obtained mixture is left to stand for 2 hours in a thermostat bath at 25° C. and then, subjected to paste extrusion through an orifice having a diameter of 2.5 cm, a land length of 1.1 cm and an introduction angle 30°, at 25° C. under conditions of a reduction ratio (ratio of the cross-sectional area of the inlet to the cross-sectional area of the outlet of a die) of 100 and an extrusion speed of 51 cm/min., to obtain an extruded bead, whereby the pressure required for the extrusion is measured, and the measured value is adopted as the extrusion pressure (unit: MPa).

### Claim 9 (depends on 5)

A production method for a stretched porous body of modified polytetrafluoroethylene, which comprises producing a fine powder of modified polytetrafluoroethylene by the method as defined in claim 5, subjecting the obtained fine powder of modified polytetrafluoroethylene to paste extrusion to obtain an extruded bead, and stretching the extruded bead.

### Claim 10 (depends on 9)

The production method for a stretched porous body of modified polytetrafluoroethylene according to claim 9, wherein the breaking strength of the stretched porous body of modified polytetrafluoroethylene is from 36 to 60N.