Manufacturing method of mechanical component using martensitic stainless steel, rotating device, rolling bearing and rolling bearing unit

A rotating device which is a mechanical component made of a martensitic stainless steel having high hardness and high corrosion resistance and manufactured by a manufacturing method, the method comprising:

• a step of preparing a martensitic stainless steel containing, by mass %, C:
• 0.20% to 0.28%, N:
• 0.1% or less, Mo:
• 3% or less, and Cr:
• 12.0% to 16.0%, such that 0.3%≤C+N≤0.4% and a PI value (═Cr+3.3Mo+16N) is 18 or more, with the remainder of substantially Fe and unavoidable impurities;
• a step of quenching said steel from a temperature of 1,030 to 1,140° C. in a vacuum furnace;
• a step of a subzero treatment of said steel;
• and a step of tempering said steel at 150° C. or lower, so as to obtain a prior austenite crystal grain size of a surface layer of 30 μm to 100 μm and a surface hardness of 58 HRc to 62 HRc,
• wherein corrosion resistance is enhanced to enable the rotating device to be exposed to a corrosive environment.