Resin composition for an exterior material of vehicle and molded product for vehicle including the same

A molded product for an exterior material of a vehicle comprising a resin composition, wherein the resin composition comprises:

• an amount of about 40 to 90 parts by weight of a polypropylene resin having a melt index of about 70 to 110 g/10 min as measured by ASTM D1238 at a temperature of 230° C. under a load of 2.16 kg;
• an amount of about 10 to 40 parts by weight of an olefin block copolymer comprising an ethylene-based repeating unit and a α-olefin-based repeating unit having 4 to 30 carbon atoms;
• an amount of about 10 to 20 parts by weight of a needle-shaped inorganic filler having an aspect ratio of about 5 to 10 according to the following Equation 1;
• and
• Aspect ratio=average length/average diameter, [Equation 1]
• an amount of about 0.01 to 5 parts by weight of a laser-transmitting black colorant selected from the group consisting of a phthalocyanine-based dye, a dioxazine-based dye, and a benzoimidazolone-based dye and a combination thereof,
• wherein all the parts by weights based on 100 parts by weight of the resin composition,
• wherein the molded product has a thickness of about 1.5 to 2.5 mm,
• wherein the molded product has i) an average transmittance in a wavelength of about 380 to 700 nm ranging from about 0.01 to 1% or less, and ii) an average transmittance in a wavelength band of about 800 to 1200 nm ranging from about 15% or greater and less than 100%.