Pneumatic tire

A pneumatic tire, formed from a rubber composition, the rubber composition comprising:

• a rubber component comprising natural rubber, styrene-butadiene rubber and polybutadiene rubber;
• carbon black having a nitrogen adsorption specific surface area of 140 m2/g to 190 m2/g;
• and
• silica,
• wherein
• an amount of the natural rubber based on 100% by mass of the rubber component is 50 to 90% by mass,
• an amount of the styrene-butadiene rubber based on 100% by mass of the rubber component is 5 to 40% by mass,
• an amount of the polybutadiene rubber based on 100% by mass of the rubber component is 5 to 40% by mass,
• an amount of the carbon black per 100 parts by mass of the rubber component is 50 to 70 parts by mass,
• an amount of the silica per 100 parts by mass of the rubber component is 30 to 50 parts by mass, and
• the rubber composition has an elongation at break of 540% or higher as measured under the following test conditions:
• Tensile rate:
• 8.3 m/sec,
• Temperature:
• 75° C.,
• Specimen:
• No. 3 dumbbell.