# US 10,770,734 B2 · Lithium air battery and manufacturing method therefor > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 10,770,734 B2 - Document ID: US10770734B2 - Status: Granted - Kind: B2 - Application number: 15/559,919 - Filed: 2016-08-12 - Published: 2018-03-15 - Granted: 2020-09-08 - Earliest claimed: 2015-08-14 - Assignees: LG Chem, Ltd. - Applicants: LG Chem, Ltd. - Inventors: Eunkyung Cho; Kwonnam Sohn; Jonghyun Chae; Doo Kyung Yang - Web page: https://patentgrep.com/patent/US10770734B2 ## CPC - H01M 4/96: Carbon-based electrodes - H01M 4/382: {Lithium (H01M4/405 takes precedence)} - H01M 4/8605: {Porous electrodes} - H01M 4/8647: {consisting of more than one material, e.g. consisting of composites} - H01M 4/88: Processes of manufacture - H01M 4/8807: {Gas diffusion layers} - H01M 12/02: Details (of electrodes H01M4/00; of non-active parts H01M50/00) - H01M 12/08: composed of a half-cell of a fuel-cell type and a half-cell of the secondary-cell type - H01M 50/417: Polyolefins - H01M 50/437: Glass - H01M 50/44: Fibrous material - H01M 2220/20: Batteries in motive systems, e.g. vehicle, ship, plane - H01M 2300/0028: characterised by the solvent - Y02E 60/10: Energy storage using batteries - H01M: PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY - Y02E: REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION ## Abstract The present invention relates to a lithium air battery and a method of manufacturing the same, wherein the lithium air battery comprises; a positive electrode which uses oxygen as an anode active material and is formed by laminating carbon black secondary particles which are composed of carbon black primary particles and graphene, and including macropores having a pore size range of exceeding 100 nm formed between the carbon black secondary particles; a negative electrode disposed to face the positive electrode; and a separation membrane disposed between the positive electrode and the negative electrode. The lithium air battery provides an increase in discharge capacity in a discharge test and a decrease in overvoltage, and can be manufactured by a simple method. ## Claims ### Claim 1 A lithium air battery comprising: a positive electrode, which comprises a laminate on a gas diffusion layer, and which uses oxygen as a positive electrode active material, wherein the laminate is formed by laminating carbon black secondary particles and consists of carbon black primary particles and graphene on the gas diffusion layer, wherein pores in the positive electrode have a pore size range of exceeding 100 nm formed between the carbon black secondary particles, and wherein the carbon black secondary particles comprise 7.4 to 44.4 wt % graphene; a negative electrode disposed to face the positive electrode; and a separator disposed between the positive electrode and the negative electrode, wherein the carbon black secondary particles are spherical and have a diameter greater than 500 nm to 10 μm or less. ### Claim 2 (depends on 1) The lithium air battery according to claim 1, wherein the carbon black primary particles are spherical and have a diameter of 1 nm to 500 nm, and the graphene has plate-shaped in the size of 0.1 μm to 500 μm and in the thickness of 0.34 nm to 20 nm. ### Claim 3 (depends on 2) The lithium air battery according to claim 2, wherein the carbon black secondary particles have structure that the plate-shaped graphene is surrounded by the spherical carbon black primary particles, and on a surface of the carbon black secondary particles, an area occupied by the spherical carbon black primary particles is larger than that occupied by the plate-shaped graphene. ### Claim 4 (depends on 1) The lithium air battery according to claim 1, wherein the carbon black secondary particles are prepared by dispersing the carbon black primary particles and the graphene in a solvent and then spray-drying them. ### Claim 5 (depends on 1) The lithium air battery according to claim 1, wherein the carbon black secondary particles include the pores having a pore size range of 20 to 100 nm formed between the carbon black primary particles and the graphene, the pores having a pore size range of less than 10 nm formed inside the carbon black primary particles, and the pores having a pore size range of less than 10 nm formed inside the graphene. ### Claim 6 (depends on 1) The lithium air battery according to claim 1, wherein the carbon black is one selected from the group consisting of ketjen black, super p, denka black, acetylene black, furnace black, and mixtures thereof. ### Claim 7 (depends on 1) The lithium air battery according to claim 1, wherein the graphene is one selected from the group consisting of graphene plate (GNP), graphene oxide (GO), reduced graphene oxide (rGO), and mixtures thereof. ### Claim 8 (depends on 1) The lithium air battery according to claim 1, wherein the positive electrode has an average pore size measured by mercury porosimetry is exceeding 100 nm to 10 μm or less. ### Claim 9 (depends on 1) The lithium air battery according to claim 1, wherein the gas diffusion layer comprises one active material selected from the group consisting of carbon cloth, carbon paper, carbon felt, an oxygen-selective permeable membrane, and mixtures thereof. ### Claim 10 (depends on 1) The lithium air battery according to claim 1, wherein the separator comprises one selected from the group consisting of polyethylene membrane, polypropylene membrane and glass fiber membrane. ### Claim 11 (depends on 1) The lithium air battery according to claim 1, wherein the lithium air battery further comprises one electrolyte selected from the group consisting of aqueous electrolyte, non-aqueous electrolyte, organic solid electrolyte, inorganic solid electrolyte, and mixtures thereof. ### Claim 12 (depends on 1) A method of manufacturing a lithium air battery according to claim 1, which comprises the steps of dispersing the carbon black primary particles in a solvent to prepare a first dispersion; dispersing the graphene in a solvent to prepare a second dispersion; mixing the first dispersion and the second dispersion to prepare a slurry; spray-drying the slurry to prepare the carbon black secondary particles; and laminating the carbon black secondary particles on the gas diffusion layer to prepare the positive electrode. ### Claim 13 (depends on 12) The method of manufacturing a lithium air battery according to claim 12, wherein the step of spray-drying the slurry is carried out by spraying the slurry through a nozzle to form droplets in the size range of 10 to 500 μm and by removing the solvent of the droplets. ### Claim 14 (depends on 12) The method of manufacturing a lithium air battery according to claim 12, wherein the carbon black secondary particles are applied to the gas diffusion layer in the amount of 0.1 to 10 mg/cm2.