# US 10,767,038 B2 · Rubber modified vinyl-based graft copolymer, and thermoplastic resin composition containing same > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 10,767,038 B2 - Document ID: US10767038B2 - Status: Granted - Kind: B2 - Application number: 15/766,927 - Filed: 2016-12-13 - Published: 2018-10-18 - Granted: 2020-09-08 - Earliest claimed: 2015-12-31 - Assignees: Lotte Advanced Materials Co., Ltd. - Applicants: Lotte Advanced Materials Co., Ltd. - Inventors: Joo Hyun Jang; Yu Jin Jung; Ki Bo Chang; Jeong Tae Kim; Kwang Soo Park - Web page: https://patentgrep.com/patent/US10767038B2 ## CPC - C08L 51/04: grafted on to rubbers - C08F 226/00: Copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a single or double bond to nitrogen or by a heterocyclic ring containing nitrogen - C08F 279/04: Vinyl aromatic monomers and nitriles as the only monomers - C08L 9/02: Copolymers with acrylonitrile - C08L 25/12: with unsaturated nitriles - C08F 2500/12: Melt flow index or melt flow ratio - C08L 2205/025: containing two or more polymers of the same hierarchy C08L, and differing only in parameters such as density, comonomer content, molecular weight, structure - C08L 2205/035: containing four or more polymers in a blend - C08L 2207/04: Thermoplastic elastomer - C08L 2207/53: Core-shell polymer - C08L: COMPOSITIONS OF MACROMOLECULAR COMPOUNDS (compositions based on polymerisable monomers C08F, C08G; artificial filaments or fibres D01F; textile treating compositions D06) - C08F: MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS ## Abstract A rubber modified vinyl-based graft copolymer of the present invention has a core-shell structure in which a shell is formed by graft-polymerizing a monomer mixture to a core comprising a rubbery polymer, wherein the monomer mixture comprises: an aromatic monomer comprising an α-substituted aromatic vinyl-based monomer represented by chemical formula 1 and an aromatic vinyl-based monomer excluding the α-substituted aromatic vinyl-based monomer; a cyanovinyl-based monomer; and a maleimide-based monomer. A thermoplastic resin composition containing the rubber modified vinyl-based graft copolymer has excellent impact resistance, heat resistance, appearance characteristics and the like. ## Claims ### Claim 1 A thermoplastic resin composition comprising: a rubber-modified vinyl-based graft copolymer having a core-shell structure, in which a shell is formed by graft polymerization of a monomer mixture to a core comprising a rubber polymer, wherein the monomer mixture comprises about 30 wt % to about 80 wt % of an aromatic monomer comprising an alpha position-substituted aromatic vinyl-based monomer represented by Formula 1 and an aromatic vinyl-based monomer other than the alpha position-substituted aromatic vinyl-based monomer, wherein the alpha position-substituted aromatic vinyl-based monomer and the aromatic vinyl-based monomer other than the alpha position-substituted aromatic vinyl-based monomer are present in a weight ratio of about 0.5:1 to about 5:1; about 10 wt % to about 30 wt % of a vinyl cyanide-based monomer; and about 10 wt % to about 30 wt % of a maleimide-based monomer: wherein R1 is a C1 to C5 alkyl group and Ar is a substituted or unsubstituted C6 to C20 aryl group or a substituted or unsubstituted C7 to C20 alkylaryl group; and an aromatic vinyl-based copolymer resin, wherein the thermoplastic resin composition has an Izod impact strength of about 20 kgf·cm/cm to about 40 kgf·cm/cm, as measured on a ¼″ thick specimen in accordance with ASTM D256, a melt-flow index of about 3 g/10 min to about 5 g/10 min, as measured at 200° C. under a load of 10 kg in accordance with ISO 1133, and a Vicat softening temperature (VST) of about 110° C. to about 130° C., as measured under a load of 5 kg in accordance with ASTM D1525. ### Claim 2 (depends on 1) The thermoplastic resin composition according to claim 1, wherein the thermoplastic resin composition comprises about 10 wt % to about 40 wt % of the rubber-modified vinyl-based graft copolymer and about 60 wt % to about 90 wt % of the aromatic vinyl-based copolymer resin. ### Claim 3 (depends on 1) The thermoplastic resin composition according to claim 1, wherein the aromatic vinyl-based copolymer resin comprises a copolymer of an aromatic monomer and a vinyl cyanide-based monomer; a copolymer of a vinyl cyanide-based monomer and an aromatic monomer comprising an alpha position-substituted aromatic vinyl-based monomer and an aromatic vinyl-based monomer other than the alpha position-substituted aromatic vinyl-based monomer; and/or a copolymer of an aromatic monomer, a vinyl cyanide-based monomer, and a maleimide-based monomer. ### Claim 4 (depends on 1) The thermoplastic resin composition according to claim 1, wherein the rubber-modified vinyl-based graft copolymer is prepared by graft copolymerization of about 60 to about 160 parts by weight of the shell relative to about 100 parts by weight of the core. ### Claim 5 (depends on 1) The thermoplastic resin composition according to claim 1, wherein the rubber polymer of the rubber-modified vinyl-based graft copolymer has an average particle diameter of about 200 nm to about 400 nm. ### Claim 6 (depends on 1) The thermoplastic resin composition according to claim 1, wherein the core of the rubber-modified vinyl-based graft copolymer is formed by polymerization of an aromatic monomer and a vinyl cyanide-based monomer swollen into the rubber polymer. ### Claim 7 (depends on 6) The thermoplastic resin composition according to claim 6, wherein the wherein the core is formed by polymerization of about 10 to about 110 parts by weight of the aromatic monomer and the vinyl cyanide-based monomer relative to about 100 parts by weight of the rubber polymer, and the aromatic monomer and the vinyl cyanide-based monomer are present in a weight ratio of about 1.5:1 to about 4:1. ### Claim 8 (depends on 1) The thermoplastic resin composition according to claim 1, wherein the maleimide-based monomer comprises a compound represented by Formula 2: wherein R2 is a C1 to C20 hydrocarbon group.