Polymer polyols comprising amine based polyether polyols and a process for preparing these polymer polyols
AssigneeCovestro LLC
InventorRick L. Adkins
Life of this patent
Estimating the term…
Abstract
This invention relates to polymer polyols which comprise one or more base polyols, at least one preformed stabilizer, one or more ethylenically unsaturated monomers, and, in the presence of at least one free radical polymerization catalyst, and optionally, one or more polymer control agents. The base polyol of these polymer polyols comprises one or more amine initiated polyols. The present invention also relates to processes for preparing these polymer polyols, to foams prepared from these polymer polyols, and to processes for producing foams from these polymer polyols.
Claims14
A polymer polyol having a solids content greater than about 15% by weight and less than 30% by weight, based on the total weight of the polymer polyol, and comprising the free-radical polymerization product of:
- (a) one or more base polyols comprising at least one of
- (I) a blend comprising
- (1) one or more amine initiated polyols wherein the amine initiator is free of tertiary amine groups and said amine initiated polyols have an equivalent weight of less than 500,
- and
- (2) one or more hydroxyl initiated polyols having a functionality of from about 2 to about 8 and a hydroxyl number of from about 10 to about 1000, wherein said hydroxyl initiated polyols are selected from the group consisting of polyether polyols, polyester polyols, polyetherester polyols and mixtures thereof;
- or
- (II) one or more amine initiated polyols wherein the amine initiator comprises an alkanolamine and is free of tertiary amine groups, and said amine initiated polyols have an equivalent weight of less than 500;
- (b) at least one preformed stabilizer further comprising a polymer control agent;
- and
- (c) one or more ethylenically unsaturated monomers;
- combined in the presence of
- (d) at least one free radical polymerization catalyst;
- and, in the absence of
- (e) additional polymer control agent which is added separately from the preformed stabilizer.
A process for the preparation of a polymer polyol having a solids content greater than about 15% by weight and less than 30% by weight, based on the total weight of the polymer polyol, comprising
- (I) free-radically polymerizing:
- (a) one or more base polyols comprising at least one of
- (I) a blend comprising
- (1) one or more amine initiated polyols wherein the amine initiator is free of tertiary amine group and said amine initiated polyols have an equivalent weight of less than 500,
- and
- (2) one or more hydroxyl initiated polyols having a functionality of from about 2 to about 8 and a hydroxyl number of from about 10 to about 1000, wherein said hydroxyl initiated polyols are selected from the group consisting of polyether polyols, polyester polyols, polyetherester polyols and mixtures thereof;
- or
- (II) one or more amine initiated polyols wherein the amine initiator comprises an alkanolamine and is free of tertiary amine groups, and said amine initiated polyols have an equivalent weight of less than 500:
- (b) at least one preformed stabilizer further comprising a polymer control agent;
- and
- (c) one or more ethylenically unsaturated monomers;
- combined in the presence of
- (d) at least one free radical polymerization catalyst;
- and, in the absence of
- (e) additional polymer control agent which is added separately from the preformed stabilizer.