Composite fluorescent gold nanoclusters with high quantum yield and method for manufacturing the same
AssigneeChung Yuan Christian University
InventorsCheng-An Lin, Cheng-Yi Huang, Chia-Hui Lin, Tzu-Yin Hou
Life of this patent
Estimating the term…
Abstract
Disclosed herein are composite fluorescent gold nanoclusters with high quantum yield, as well as methods for manufacturing the same. According to some embodiments, the composite fluorescent gold nanocluster includes a gold nanocluster and a capping layer that encapsulates at least a portion of the outer surface of the gold nanocluster. The capping layer includes a matrix made of a benzene-based compound, and multiple phosphine-based compounds distributed across the matrix.
Claims10
A method of producing composite fluorescent gold nanoclusters, comprising,
- (a) mixing gold(III) chloride (AuCl3) and a benzene-based compound in a molar ratio of 1:0.5 to 1:5 to produce a first fluorescent gold nanoclusters;
- and
- (b) treating the first fluorescent gold nanoclusters with an energy source selected from the group consisting of UV, acoustic, heat, microwave and a combination thereof to produce a second fluorescent gold nanoclusters;
- and
- (c) modifying the second fluorescent gold nanoclusters of the step (b) with a phosphine-based compound to produce the composite fluorescent gold nanoclusters;
- wherein,
- wherein, the method is characterized in not using any reducing agent;
- the first and second fluorescent gold nanoclusters respectively emit blue and yellow light;
- and
- the composite fluorescent gold nanoclusters independently emit yellow or green light with the peak emission wavelength ranges from 500 nm to 580 nm.
A method of producing composite fluorescent gold nanoclusters, comprising, (a) mixing gold(III) chloride (AuCl3), a benzene-based compound, and a phosphine-based compound in a molar ratio of 1:0.5:0.1 to 1:5:20 to produce fluorescent gold nanoclusters;
- and (b) treating the fluorescent gold nanoclusters with an energy source selected form the group consisting of UV, acoustic wave, heat, microwave and a combination thereof to produce the composite fluorescent gold nanoclusters;
- wherein, the method is characterized in not using any reducing agent;
- and the composite fluorescent gold nanoclusters independently emit yellow or green light with the peak emission wavelength ranges from 500 nm to 580 nm.