Sheet for shoe sole and shoe sole including the same

A process for producing a molded composite article as a shoe sole, which comprises

• directly forming a crosslinked rubber layer at a first side of a sheet and directly forming a thermoplastic elastomer layer at a second side of the sheet,
• wherein a molten uncrosslinked rubber composition is contacted with the first side of the sheet in a metal mold, and the uncrosslinked rubber composition is crosslinked under heating to form the crosslinked rubber layer, wherein the uncrosslinked rubber composition is crosslinked without melting the sheet and the crosslinked rubber layer is formed without opening the metal mold,
• wherein the sheet comprises a resin component (A) containing a polyamide resin (a), the polyamide resin (a) comprising at least one member selected from the group consisting of a polyamide (a-1) and a polyamide elastomer (a-2),
• the resin component (A) is any one of the following (1) and (2):
• (1) the polyamide resin (a) consisting essentially of the polyamide elastomer (a-2) having an amino group concentration of not less than 10 mmol/kg, a melting point of not lower than 165° C., and a flexural modulus of not less than 300 MPa in accordance with ISO178,
• (2) a resin composition comprising the polyamide (a-1) and the polyamide elastomer (a-2), wherein the polyamide elastomer (a-2) has an amino group concentration of not less than 10 mmol/kg, not less than 30% by weight of the polyamide (a-1) and/or the polyamide elastomer (a-1) has a melting point of not lower than 165° C., the resin composition satisfies, as a whole, an amino group concentration of not less than 10 mmol/kg and a flexural modulus of not less than 300 MPa in accordance with ISO178,
• wherein the thermoplastic elastomer layer comprises at least one member selected from the group consisting of a polyurethane elastomer and a polyamide elastomer, and
• wherein the uncrosslinked rubber composition comprises an uncrosslinked rubber, a crosslinking agent, and a crosslinking auxiliary, the uncrosslinked rubber comprising a non-acid-modified rubber,
• the crosslinking agent comprising a peroxide, and
• the crosslinking auxiliary comprising at least one member selected from the group consisting of a trifunctional or polyfunctional (meth)acrylate and an aromatic bismaleimide, and
• the amount of the crosslinking auxiliary is about 0.1 to 10 parts by weight relative to the 100 parts by weight of the uncrosslinked rubber.

A molded composite article configured as a shoe sole, said article comprising a sheet having a thickness of 0.1 to 0.7 mm, a crosslinked rubber layer as a stud directly laminated on and bonded to a first side of the sheet, and a thermoplastic elastomer layer comprising at least one member selected from the group consisting of a polyurethane elastomer and a polyamide elastomer as a sole directly laminated on and bonded to a second side of the sheet,

• wherein the sheet comprises a resin component (A) which is a polyamide resin consisting essentially of a polyamide elastomer having an amino group concentration of not less than 10 mmol/kg, a melting point of not lower than 165° C., and a flexural modulus of not less than 300 MPa in accordance with ISO178, wherein the resin component (A) has an amino group concentration of 10 to 100 mmol/kg, and
• wherein the crosslinked rubber layer is a crosslinked layer of an uncrosslinked rubber composition comprising:
• an uncrosslinked rubber comprising a non-acid-modified rubber;
• a peroxide crosslinking agent;
• and a crosslinking auxiliary comprising at least one member selected from the group consisting of a trifunctional or polyfunctional (meth)acrylate and an aromatic bismaleimide, with the amount of the crosslinking auxiliary being about 0.1 to 10 parts by weight relative to the 100 parts by weight of the uncrosslinked rubber.