Method for preparing spherical celluloid beads
AssigneeThe United States of America as represented by the Secretary of the Army
InventorsSubhash Patel, Viral Panchal, Ming-Wan Young
Life of this patent
Estimating the term…
Abstract
A wet chemistry method for preparing spherical celluloid beads by mixing a water-based suspension solution and a solvent based celluloid solution that is immiscible in the suspension solution. The two combined solutions create an “oil-in-water” type mixture where the dispersed phase consists of celluloid dissolved in solvent and co-solvent that is suspended in the continuous water phase. Agitation and removal of the solvent and co-solvent mixture produces spherical shaped celluloid beads.
Claims8
A method of preparing solid, spherical celluloid beads comprising:
- a. preparing a suspension solution consisting essentially of water and gelatin wherein the gelatin is dissolved in the water and the density of the suspension solution is about 1.1 g/cm3 to 1.2 g/cm3 compared to water at 1.0 g/cm3;
- b. preparing a celluloid solution comprising celluloid in a solvent and adding a co-solvent to adjust the density of the celluloid solution to about 1.1 g/cm3 to 1.59 g/cm3, compared to water at 1.0 g/cm3, wherein the density of the celluloid solution is equal to or greater than the density of the suspension solution, wherein the celluloid is dissolved in the solvent and the co-solvent, and wherein the solvent and the co-solvent are miscible with each other, immiscible in water, and have a boiling point lower than water;
- c. adding the celluloid solution to the suspension solution to form droplets of the celluloid wherein the droplets of the celluloid are suspended in the suspension solution to create a system;
- d. agitating the system to create an agitated system comprising droplets of the celluloid suspended in the suspension solution;
- wherein the droplets of the celluloid are spherical;
- and
- e. heating the agitated system to between 25° C. and less than the boiling point of water to remove the solvent and the co-solvent from the agitated system to form solid, spherical celluloid beads wherein the diameter of the solid, spherical celluloid beads is about 0.14 mm to 1.02 mm.
A method of preparing solid, spherical celluloid heads comprising:
- a. preparing a suspension solution consisting essentially of water and gelatin wherein the gelatin is dissolved in the water and the density of the suspension solution is about 1.1 g/cm3 to 1.2 g/cm3 compared to water at 1.0 g/cm3;
- b. preparing a celluloid solution comprising celluloid in ethyl acetate and adding carbon tetrachloride to adjust the density of the celluloid solution to about 1.1 g/cm3 to 1.59 g/cm3 compared to water at 1.0 g/cm3, wherein the density of the celluloid solution is equal to or greater than the density of the suspension solution;
- c. adding the celluloid solution to the suspension solution to create a mixture;
- d. agitating the mixture to form an agitated mixture comprising spherical droplets of the celluloid suspended in the suspension solution;
- and
- e. heating the agitated mixture to remove the ethyl acetate and carbon tetrachloride from the agitated mixture to form solid, spherical celluloid beads in the suspension solution wherein the diameter of the solid, spherical celluloid beads is about 0.4 mm to 1.02 mm;
- and
- f. isolating the solid, spherical celluloid beads from the suspension solution.
Dependencies are inferred from the claim text.