Method of manufacturing intramedullary nails made of chitosan for long bones fractures treatment

A method for manufacturing of intramedullary nails made of chitosan for fracture treatments of long bones, consisting of the following steps:

• a) preparing powdered chitosan, obtained in deacetylation process of chitin from marine organisms;
• b) dissolving the powdered chitosan in water to obtain a 5% chitosan solution into which a 70-90% acetic acid is added, while stirring, until a uniform chitosan solution is obtained;
• c) coating the inner surface of a mold with said uniform chitosan solution and filling the thus formed coated mold with a coagulation bath of 5% aqueous solution of NaOH to obtain a gel die;
• d) removing the coagulation bath from the gel die and filling the gel die with the uniform chitosan solution obtained in step (b), and subsequently subjecting the filled gel die to a coagulation bath of 5% aqueous solution of NaOH and thus forming a blank intramedullary nail in the gel die;
• e) subjecting the blank intramedullary nail obtained in step (d) to a neutralizing bath of deionized water to a pH of 6.5-7.5 after the coagulation bath is removed,
• f) subjecting the blank intramedullary nail obtained in step (e) to a crosslinking bath in a solution formed from 0.5 to 2% of sodium tripolyphosphate and 0.5% to 3% Na3PO4 for 24 to 48 hours at a temperature of 50° C. to 140° C.;
• g) subjecting the blank intramedullary nail obtained in step (f) to a drying process for a period of 6 to 10 days, thus obtaining a dry blank intramedullary nail having flexural strength (W) of 130 MPa and flexural modulus (E) of 2.6 GPa;
• and
• h) treating a surface of the dry blank intramedullary nail obtained in step (g) to form an intramedullary nail, wherein the surface treatment is carried out until the surface of the intramedullary nail contains at least 20%-40% of pores having a depth of 0.1 mm to 1 mm.