Thermal sensing layer for microbolometer and method of making the same

Abstract

The thermal sensing layer for a microbolometer includes a Ge1-xSnx film layer, where 0.17≤x≤0.25. The Ge1-xSnx film layer may be deposited on a substrate layer, such as pure silicon. An additional layer of silicon dioxide may be added, such that the silicon dioxide layer is sandwiched between the silicon substrate and the Ge1-xSnx film. In order to make the Ge1-xSnx thin film layer, germanium (Ge) and tin (Sn) are simultaneously sputter deposited on the substrate, where the atomic ratio of germanium to tin is between 0.83:0.17 and 0.75:0.25 inclusive. The sputter deposition may occur in an argon atmosphere, with the germanium having a deposition rate of 9.776 nm/min, and with the tin having a deposition rate between 2.885 nm/min and 4.579 nm/min.