Fiber-reinforced thermoplastic resin molded article, and fiber-reinforced thermoplastic resin molding material

A fiber reinforced thermoplastic resin molding material comprising:

• 5 to 45 parts by weight of carbon fibers (A);
• 1 to 45 parts by weight of organic fibers (B);
• 10 to 94 parts by weight of a thermoplastic resin (C);
• and 1 to 25 parts by weight of a compound (D) having a melt viscosity at 200° C. that is lower than that of the thermoplastic resin (C), based on 100 parts by weight of the total amount of the carbon fibers (A), the organic fibers (B), and the thermoplastic resin (C), wherein:
• the organic fibers (B) have a number average fiber diameter (dB) of 1 to 10 μm;
• the thermoplastic resin (C) is contained at an outer side of a composite (F) obtained by impregnating a fiber bundle (E) comprising the carbon fibers (A) and the organic fibers (B) with the compound (D);
• the carbon fibers (A) and the organic fibers (B) are unevenly distributed in a cross section of the fiber bundle (E);
• and
• the length of the fiber bundle (E) and the length of the fiber reinforced thermoplastic resin molding material are substantially the same.

A fiber reinforced thermoplastic resin molding material comprising:

• a carbon fiber reinforced thermoplastic resin molding material (X) comprising 5 to 45 parts by weight of carbon fibers (A), 35 to 94 parts by weight of a thermoplastic resin (C), and 1 to 25 parts by weight of a compound (D) having a melt viscosity at 200° C. that is lower than that of the thermoplastic resin (C), based on 100 parts by weight of the total amount of the carbon fibers (A), the thermoplastic resin (C), and the compound (D) having a melt viscosity at 200° C. that is lower than that of the thermoplastic resin (C), wherein the thermoplastic resin (C) is contained at an outer side of a composite (G) obtained by impregnating the carbon fibers (A) with the compound (D), and the length of the carbon fibers (A) and the length of the carbon fiber reinforced thermoplastic resin molding material are substantially the same;
• and
• an organic fiber reinforced thermoplastic resin molding material (Y) comprising 1 to 45 parts by weight of organic fibers (B), 35 to 94 parts by weight of a thermoplastic resin (H), and 1 to 25 parts by weight of a compound (I) having a melt viscosity at 200° C. that is lower than that of the thermoplastic resin (H), based on 100 parts by weight of the total amount of the organic fibers (B), the thermoplastic resin (H), and the compound (I), wherein the organic fibers (B) have a number average fiber diameter (dB) of 1 to 10 μm.