High permeability magnetic sheet
AssigneeTDK Corporation
InventorsAtsuhito Matsukawa, Yoshihiro Honjo, Mitsuhiro Matsuhashi
Life of this patent
Estimating the term…
Abstract
A magnetic sheet comprises, by vol. %, Fe—Si—Al alloy flat powder: 36% or more. The Fe—Si—Al alloy flat powder comprises, by wt %, 9.3%≤Si≤9.7%, 5.7%≤Al≤6.1%, and remaining Fe. The Fe—Si—Al alloy flat powder has: an aspect ratio in a range of 20 or more and 50 or less; a 50% particle size D50 in a range of 50 μm or more and 100 μm or less; and a coercivity Hc of 60 A/m or less. The magnetic sheet has a temperature characteristic of permeability μ′ measured at 1 MHz exhibiting a maximum value in a range of 0° C. or more and 40° C. or less.
Claims1
A magnetic sheet comprising, by vol. %, Fe—Si—Al alloy flat powder:
- 36% or more, the Fe—Si—Al alloy flat powder (i) comprising, by wt %, 9.40≤Si≤9.65, 5.7%≤Al≤6.1%, and remaining Fe, and (ii) having:
- an aspect ratio in a range of 20 or more and 50 or less;
- a 50% particle size D50 in a range of 50 μm or more and 100 μm or less;
- and
- a coercivity Hc of 60 A/m or less,
- wherein the magnetic sheet has a temperature characteristic of permeability μ′ measured at 1 MHz exhibiting a maximum value in a range of 0° C. or more and 40° C. or less.
Dependencies are inferred from the claim text.